A simple solution route to control synthesis of Fe3O4 nanomaterials at low temperature and their magnetic properties

A series of nanostructured iron compounds including cubic Fe3O4 and orthorhombic FeOOH were synthesized via a facile low temperature (in the range of 60−100°C) solution method. In the whole process, the interaction between FeCl2·4H2O and methenamine (C6H12N4) was carried out through a reflux device under different reaction conditions such as temperature, solvent, and duration. The samples were detected by XRD, TEM, SAED, physical property measurement system, and Mossbauer spectroscopy, separately. The experiments showed that magnetic mixture nanoparticles had flake and rod morphologies, and cubic Fe3O4 took on grain nanostructure. Magnetism measurements indicated that the saturated magnetization of the as-obtained magnetic mixture was lower than that of the cubic magnetite. Mossbauer spectroscopy testified the sample consisting of cubic magnetite rather than γ-Fe2O3. In addition, a possible growth mechanism of cubic magnetic nanoparticles under different conditions was discussed.