Phase formation in Zr–Fe multilayers: Effect of irradiation

We have conducted a detailed in situ study of phase formation in Zr–Fe metallic multilayers using irradiation and thermal annealing. Metallic multilayers with near equiatomic and Fe-rich overall compositions and with repetition thicknesses ranging from 7.4 to 33 nm were either irradiated with 300 keV Kr ions at various temperatures (from 17 to 623 K) or thermally annealed at 773 K while being observed in situ. The kinetics of multilayer reaction were monitored by following the diffraction patterns. For near equiatomic samples, irradiation causes complete amorphization. The dose to amorphization increases in proportion to the square of the wavelength, indicating a process controlled by atomic transport. Amorphization was also achieved by 900 keV electron irradiation at 25 K showing that displacement cascades are not required. The critical dose to amorphization was independent of temperature below room temperature and decreased above room temperature. The activation energy for this second process is 0.17 eV...