Modeling of the elastic precursor behavior and dynamic inelasticity of tantalum under ramp wave loading to 17 GPa

In a previous study by Asay et al. [J. Appl. Phys. 106, 073515 (2009)], the inelastic response of annealed and cold-rolled pure polycrystalline tantalum at intermediate strain rates was characterized with ramp wave loading to peak longitudinal stresses of 17 GPa. It was found that the annealed Ta at strain rates of about 106/s exhibited pronounced elastic overshoot, followed by rapid stress relaxation and the amplitude of the elastic precursor depicted essentially no dependence on sample thickness for samples with controlled initial properties, in contrast to the precursor attenuation typically observed in shock wave experiments. The precursor for the cold-rolled sample was more dispersive and did not exhibit the characteristics depicted by the annealed samples. A principal objective of the present study was to gain some insights into this behavior and its implication on the deformation mechanisms for tantalum. Another objective was to gain a fundamental understanding of the dynamic inelasticity of polycr...