Porous Ni3(NO3)2(OH)4 nano-sheets for supercapacitors: Facile synthesis and excellent rate performance at high mass loadings

For supercapacitors, pores in electrode materials can accelerate chemical reaction kinetics by shortening ion diffusion distances and by enlarging electrolyte/electrode interfaces. This article describes a simple one-step route for the preparation of pure-phase porous Ni3(NO3)2(OH)4 nano-sheets by directly heating a mild Ni(NO3)2 and urea solution. During heating, urea decomposed into NH3·H2O, which provided a suitable alkaline environment for the formation of Ni3(NO3)2(OH)4 nano-sheets. Meanwhile, the side product, NH4NO3, created numerous pores as a pore-forming agent. After NH4NO3 removal, the specific surface areas and pore volumes of products were boosted by ∼180-times (from 0.61 to 113.12 m2/g) and ∼90-times (from 3.40 × 10−3 to 3.17 × 10−1 m2/g), respectively. As a cathode material of supercapacitor, the porous Ni3(NO3)2(OH)4 nano-sheets exhibited a high specific capacitance of 1094 F/g at an ultrahigh mass loading of 17.55 mg/cm2, leading to an impressive areal capacitance of 19.2 F/cm2. Furthermore, a Ni3(NO3)2(OH)4 nano-sheet//commercial active carbon asymmetric supercapacitor was constructed and delivered an energy density of 33.2 Wh/Kg at a power density of 190.5 W/Kg, based on the mass of active materials on both electrodes.