The reaction of styrene oxide with organozinc compounds was studied to clarify the polymerization mechanism of styrene oxide. In the reaction with diethylzine ring scission of styrene oxide was observed to occur almost exclusively at the CH(C6H5)O-bond to form ethylzinc monoalkoxide. In the second step zinc dialkoxide was formed by the reaction of the ethylzinc monoalkoxide with styrene oxide and the dialkoxide was found to be active species for the polymerization of styrene oxide. In the reaction of styrene oxide with zinc dialkoxide both α-scission and β-scission occurred. Studies were also made for butadiene monoxide. Die Reaktion des Styroloxids mit organischen Zinkverbindungen wurde untersucht, um den Polymerisationsmechanismus von Styroloxid zu klaren. Bei der Reaktion mit Zinkdiathyl konnte eine Ringaufspaltung des Styroloxids fast ausschlieslich der CH(C6H5)O-Bindung festgestellt werden, wobei ein Zinkatylmonoalkoxid gebildet wird. Beim zweiten Schritt bildet sich Zinkdialkoxid durch Reaktion des Zinkatbylmonoalkoxides mit Styroloxid, wobei das Dialkoxid sich als das aktive Species bei der Polymerisation des Styroloxids herausstellte. Bei der Reaktion des Styroloxids mit Zinkdialkoxid erfolgte sowohl eine α-wie auch β-Spaltung. Das Butadienmonoxid wurde entsprechend untersucht.