Migração de molibdênio na interface matriz/precipitado em metais de solda de ligas Ni-Cr-Mo

This work evaluates the chemistry elements distribution on matrix/precipitate interface in a Ni-Cr-Mo-W alloy weld metals deposited on substrate of C-Mn steel. Microestructural characterization was carried out through optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS) techniques. The results have shown that the presence of secondary phases precipitates in the interdendritic region. Through SEM analysis indications of migration of molybdenum around these phases are observed. These precipitates are identified as P-phase by TEM analysis. The molybdenum migration along matrix/precipitate interface is confirmed through EDS. The phenomenon of molybdenum migration is a result of a re-heating due to several welding heat cycles deposited to promote the coating layer. O presente trabalho avalia a migração de elementos químicos, especialmente o molibdênio, na interface matriz/precipitado de revestimentos de ligas Ni-Cr-Mo-W, depositados sobre substrato de aço C-Mn. A caracterização microestrutural foi realizada empregando-se as técnicas de microscopia eletrônica de varredura (MEV), microscopia eletrônica de transmissão (MET) e espectroscopia de energia dispersiva de raios X (EDS). Indícios de empobrecimento de molibdênio ao redor das fases secundárias são observados nas análises por MEV. Tais fases foram identificadas por MET como fase P. Análises de MET/EDS confirmam haver uma migração de molibdênio da matriz em direção aos precipitados. Comportamento semelhante é observado para o tungstênio. O fenômeno de migração de molibdênio e tungstênio é observado em cordões de solda que foram reaquecidos devido aos inúmeros ciclos térmicos de soldagem para a formação da camada de revestimento.