Bioceramics Based on Calcium Pyrophosphate

Ceramic samples based on b-calcium pyrophosphate b-Ca2P2O7 were prepared using firing at 900, 1000, and 1100 oC from powders of g-calcium pyrophosphate g-Ca2P2O7 with preset molar ratios Ca/P=1; 0,975 and 0,95. To prepare powders of g-calcium pyrophosphate g-Ca2P2O7 with preset molar ratio Ca/P=1; 0,975 and 0,95 powder mixtures based on calcium lactate pentahydrate Ca(C3H5O3)2⋅5H2O and, monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O were treated in an aqua medium in mechanical activation conditions, dried, disaggregated in acetone, and heat-treated at 600 oC. The phase composition of powder mixtures after treatment if planetary mill in aqua medium included both brushite CaHPO4⋅2H2O or monetite CaHPO4, and starting salts. The phase composition of all powder mixtures after disaggregation in acetone in planetary mill included monetite CaHPO4 and starting salts. After heat treatment at 600 oC according to the XRD data phase composition of all powder mixtures was presented by g-calcium pyrophosphate g-Ca2P2O7. The grain size of ceramics increased both with the growth of firing temperature and with decreasing of molar ratio Ca/P of powder mixtures. Calcium polyphosphate (t melt =960–968 oC) formed from monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O acted like a liquid phase sintering additive. It was confirmed by tests in vitro, that prepared ceramic materials with preset molar ratio Ca/P=1; 0,975 and 0,95 and phase composition presented by b-calcium pyrophosphate b-Ca2P2O7 according to XRD data were biocompatible and could maintain bone cells proliferation.