Safety and In Situ Antierosive Effect of CaneCPI-5 on Dental Enamel

The sugarcane cystatin (CaneCPI-5) was recently cloned and showed strong binding force to dental enamel and protection against initial erosion. However, evaluations on its safety and efficacy in a situation closer to the clinical condition are necessary. In the present study we analyzed 1) the cytotoxicity of CaneCPI-5 on human gingival fibroblasts (HGFs); 2) the ability of CaneCPI-5 to reduce enamel erosion and erosion+abrasion in situ. In part 1, HGFs were treated with CaneCPI-5 (0.025, 0.05, 0.1, 0.5 or 1.0 mg/mL) or no treatment (control). The cytotoxicity was assessed after 60 s and 24 h by mitochondrial activity (MTT), confocal microscopy, and hematoxylin/eosin staining. In part 2, 15 volunteers participated in a double-blind crossover protocol consisting of 3 phases, according to the following treatments: 1) 0.1 mg/mL CaneCPI-5; 2) SnCl2/NaF/AmF (Elmex; positive control); 3) water (negative control). The volunteers wore an appliance containing 4 bovine enamel specimens for 5 d. Each day, the specimens were individually treated with 50 µL of the tested solutions per 60 s and then subjected to erosive challenges (0.1% citric acid, pH 2.5, for 90 s, 4 times per day). After the first and last erosive challenge each day, 2 samples were abraded (toothbrushing, 15 s). Enamel wear was measured by contact profilometry. One or two-way analysis of variance (ANOVA)/Tukey’s or Sidak’s tests ( P < 0.05) were applied. Regardless of the concentration and the experimental time, CaneCPI-5 did not decrease the cell viability compared to the negative control ( P < 0.05). Erosion+abrasion led to significantly greater wear compared to erosion only. For both conditions, the lowest wear was found for SnCl2 and CaneCPI-5, which did not differ significantly from each other, but showed significant protection when compared to the negative control. In conclusion, CaneCPI-5 is safe on HGFs and reduces enamel erosive wear to the same extent as a commercial solution used to control erosive tooth wear (ETW).