Preparation and properties of natural rubber reinforced with polydopamine-coating modified carbon nanotubes

Multi-walled carbon nanotubes (MWCNTs) were functionalized by polydopamine (PDA)-coating and mixed with natural rubber (NR) via latex compounding. Compared with pristine MWCNTs, the surface of MWCNT-PDA was covered by an amorphous and nanometer-scale PDA layer which had a large amount of oxygenic and nitric functional groups. So the MWCNT-PDA showed a perfect dispersion in NR matrix. The tensile strength of NR/MWCNT-PDA (5 phr) composites is 28.6 MPa, compared with the pure NR, which increased by 42%. For the electrical properties, when the content of MWCNTPDA or MWCNTs is 2 phr, the volume resistivity of NR/MWCNT-PDA composites falls to about 2.7·109 Ω·cm, compared with 3.3·1013 Ω·cm of NR/MWCNT composites. The thermal conductivity of NR composites increased only by 28.2% when 5 phr MWCNT-PDA was added. A model proposed by Nan was used to calculate the thermal conductivity of NR/MWCNT composites, and the calculated values were compared with the experimental values, the results showed that the interface thermal resistance is the main reason why MWCNTs could not significantly increase the thermal conductivity of natural rubber.