KONTRPLAKLARDA EĞİLME DİRENCİNE TUTKAL TÜRÜNÜN ETKİSİ

In this study was compared that the bending strenght effects in the plywoods made with okume, poplar and beech coatings when used the glues; Polyurethane (PU), Epoxy, Polyvinyl acetate (PVA) and D3.Plywoods are the okume to be 0,6 mm thick in the outer, in its sublayer the poplar to be 0,6 mm thick and in the middle, the beech to be 1,2 mm thick and so totally the coating is 3,6 mm and 0,4 mm.more the glue portion was pressed in the ordinary conditions and finally 4mm. plywoods were produced.Consequently, in this experiment, the effects of the different glues to the bending strength were seemed to be almost the same. This suggests that the effects of the different glues to the plywoods’ flexure resistance are at minimum degrees.The effect values of these glues used in our work were determined from small to great Polyvinyl Acetate
Bu çalışmada, Oküme, kavak ve kayın kaplamaları kullanılarak üretilen kontrplaklarda Poliüretan (PU), Epoxy, Polivinilasetat (PVA) ve D3 tutkalının eğilme mukavemetine etkileri karşılaştırılmıştır.Kontrplaklar, dışta 0,6 mm’lik Okoume bir alt katmanında 0,6 mm’lik kavak ve ortada 1,2 mm’lik kayın olmak üzere toplam 3,6 mm’lik kaplama ve 0,4 mm’lik tutkal payıyla normal şartlar altında (NŞA) preslenerek 4 mm’lik kontrplaklar üretilmiştir.Sonuç olarak; yapılan çalışmada kullanılan tutkal türleri eğilme direncine etki değerleri birbirine yakın çıkmıştır. Kullanılan tutkalların kontrplaklarda eğilme direncine etkilerinin minumum düzeyde olduğu görülmüştür. Bu çalışmada kullanılan tutkalların eğilme direncine etki değerleri küçükten büyüğe Polivinilasetat tutkalı (PVA) < Epoxy tutkalı < D3 tutkalı < Poliüretan tutkalı(PU) şeklinde olduğu tespit edilmiştir.