Enhanced Strengthening and Toughening of T6-Treated 7046 Aluminum Alloy through Severe Plastic Deformation

The 7046 aluminum alloy possesses a favorable fatigue property, corrosion resistance and weldability, but its moderate strength and plasticity limit its wider application and development. In the present study, severe plastic deformation (SPD) was applied prior to T6 treatment to significantly enhance the strength and toughness of the 7046 aluminum alloy. The results show that the alloy processed by four passes of equal channel angular pressing (ECAP) at 300 °C prior to T6 treatment exhibits an excellent mechanical performance, achieving an ultimate tensile strength (UTS) and elongation (EL) of 485 MPa and 19%, respectively, which are 18.6% and 375% higher than that of the T6 alloy. The mechanical properties of the alloy are further improved by an additional room temperature (RT) rolling process, resulting in a UTS of 508 MPa and EL of 23.4%, respectively. The increased presence of η′ and Al6Mn phases in the 300°C4P-R80%-T6 and 300°C4P-T6 alloys contributes to a strengthening and toughening enhancement in the SPD-processed T6 alloy. The findings from this work may shed new insights into enhancing the 7046 aluminum alloy.