One step synthesis of graphene oxide under low-temperature and its microwave reduction

The graphene oxide was prepared via one step under low-temperature with natural flake graphite as raw material. Factors affecting oxidation degree and layer spacing of graphene oxide were discussed in the process of low-temperature oxidation, such as the dosage of oxidant and oxidation time in system. The results indicate that high C-O bond and low defect structure (ID:IG=0.63) graphene oxide with the carbon and oxygen atom ratio of 1.98 can be prepared in the condition of the potassium permanganate with natural flake graphite mass ratio of 1:3, oxidation temperature of 0℃, oxidation time of 48h.This way avoids the increase of graphene oxide defects in the process of Hummers preparation due to the formation of CO2, which leads to the hexagon fracture and the absence of carbon atoms. After microwave reduction, the reduced graphene oxide with low defect is obtained, which the distance between defects(LD)is 12nm,the defect density(nD) is 2.21×1011cm-2 and the ratio of ID:IG is only 0.85 (ΓG=32.1cm-1).