µ-CT Investigation of Hydrogen-Induced Cracks and Segregation Effects in Austenitic Stainless Steel

Hydrogen can drastically degrade the mechanical properties of a variety of metallic materials. The so-called hydrogen environment embrittlement of austenitic CrNi-type steels is usually accompanied by the formation of secondary surface cracks, which can be investigated in order to assess the embrittlement process. The occurrence of hydrogen-induced cracks is often related to element segregation effects that locally impact the austenite stability. Since there is as yet a lack of investigation methods that can visualize both structures three-dimensionally, the present study investigates the imageability of hydrogen-induced cracks and element segregation structures in austenitic CrNi-steel via micro-computed tomography (CT). In order to improve the X-ray visibility of segregation structures, modified versions of the reference steel, X2CrNi18-9, that contain W and Si are designed and investigated. The investigations demonstrated that small differences in the X-ray attenuation, caused by the W or Si modifications, can be detected via CT, although segregation structures could not be imaged due to their small size scale and image noise. Hydrogen-induced cracks were characterized successfully; however, the detection of the smaller cracks is limited by the resolution capability.