Synthesis of Nano-Structured Conjugated Polymers with Multiple Micro-/Meso-Pores by the Post-Crosslinking of End-Functionalized Hyperbranched Conjugated Polymers
- Source :
- Polymers, Vol 16, Iss 9, p 1192 (2024)
- Publication Year :
- 2024
- Publisher :
- MDPI AG, 2024.
-
Abstract
- A nano-structured conjugated polymer with multiple micro-/meso-pores was synthesized by post-crosslinking of an end-functionalized hyperbranched conjugated prepolymer. Firstly, an AB2 monomer 3-((3,5-dibromo-4-(octyloxy)phenyl)ethynyl)-6-ethynyl-9-octyl-9H-carbazole (PECz) was synthesized and polymerized by Sonogashira reaction to give the -Br end-functionalized hyperbranched conjugated prepolymer hb-PPECz. The photophysical and electrochemical properties of hb-PPECz were investigated. The λmax of absorption and emission of hb-PPECz in tetrahydrofuran (THF) solution was 313 and 483 nm, respectively. The optical energy bandgap, highest occupied molecular orbital (HOMO), and lowest unoccupied molecular orbital (LUMO) energy levels of hb-PPECz were 2.98, −5.81, and −2.83 eV, respectively. Then, the prepolymer hb-PPECz was post-crosslinked by Heck reaction with divinylbenzene to give the porous conjugated polymer c-PPECz. The effects of hb-PPECz concentration and added dispersant polyvinylpyrrolidone (PVP K-30) on the morphology and porosity of c-PPECz were investigated. The resulting c-PPECzs showed multiple porous structures mainly constructed by micropores and mesopores. Under a higher hb-PPECz concentration (4 wt/v%), a bulky gel product was obtained. Under lower hb-PPECz concentrations (0.6 wt/v%~2 wt/v%), the resulting c-PPECzs were mainly composed of nano-sized particles. Nearly spheric nanoparticles (200~300 nm) (c-PPECz-5) were obtained under the concentration of 1 wt/v% in the presence of PVP (10 wt% of hb-PPECz). The Brunauer–Emmett–Teller (BET) surface area, pore volume, average pore size, and percentage of pore size below 10 nm of c-PPECz-5 were 10.7781 m2·g−1, 0.0108 cm3·g−1, 4.0081 nm, and 94.47%, respectively.
Details
- Language :
- English
- ISSN :
- 20734360
- Volume :
- 16
- Issue :
- 9
- Database :
- Directory of Open Access Journals
- Journal :
- Polymers
- Publication Type :
- Academic Journal
- Accession number :
- edsdoj.32d9cce7c66e4210afea6a529af6e939
- Document Type :
- article
- Full Text :
- https://doi.org/10.3390/polym16091192