The Effects of a Varied Gold Shell Thickness on Iron Oxide Nanoparticle Cores in Magnetic Manipulation, T1 and T2 MRI Contrasting, and Magnetic Hyperthermia

Fe3O4–Au core–shell magnetic-plasmonic nanoparticles are expected to combine both magnetic and light responsivity into a single nanosystem, facilitating combined optical and magnetic-based nanotheranostic (therapeutic and diagnostic) applications, for example, photothermal therapy in conjunction with magnetic resonance imaging (MRI) imaging. To date, the effects of a plasmonic gold shell on an iron oxide nanoparticle core in magnetic-based applications remains largely unexplored. For this study, we quantified the efficacy of magnetic iron oxide cores with various gold shell thicknesses in a number of popular magnetic-based nanotheranostic applications; these included magnetic sorting and targeting (quantifying magnetic manipulability and magnetophoresis), MRI contrasting (quantifying benchtop nuclear magnetic resonance (NMR)-based T1 and T2 relaxivity), and magnetic hyperthermia therapy (quantifying alternating magnetic-field heating). We observed a general decrease in magnetic response and efficacy with an increase of the gold shell thickness, and herein we discuss possible reasons for this reduction. The magnetophoresis speed of iron oxide nanoparticles coated with the thickest gold shell tested here (ca. 42 nm) was only ca. 1% of the non-coated bare magnetic nanoparticle, demonstrating reduced magnetic manipulability. The T1 relaxivity, r1, of the thick gold-shelled magnetic particle was ca. 22% of the purely magnetic counterpart, whereas the T2 relaxivity, r2, was 42%, indicating a reduced MRI contrasting. Lastly, the magnetic hyperthermia heating efficiency (intrinsic loss power parameter) was reduced to ca. 14% for the thickest gold shell. For all applications, the efficiency decayed exponentially with increased gold shell thickness; therefore, if the primary application of the nanostructure is magnetic-based, this work suggests that it is preferable to use a thinner gold shell or higher levels of stimuli to compensate for losses associated with the addition of the gold shell. Moreover, as thinner gold shells have better magnetic properties, have previously demonstrated superior optical properties, and are more economical than thick gold shells, it can be said that “less is more”.