Influence of PA66 fiber content on porosity of porous aluminum based ceramic core

In order to solve the problem that alumina based ceramic core is not easy to remove core, a certain amount of PA66 fiber was added as pore forming material to prepare porous aluminum based ceramic core by hot pressing. The influence of PA66 fiber content on the porosity, room temperature bending strength and sintering shrinkage of aluminum based ceramic core was investigated, and the mechanism of PA66 fiber content on the porosity of aluminum based ceramic core was analyzed. The results show that the porosity of alumina based ceramic core is significantly increased by adding PA66 fiber, and the sintering shrinkage of the core is effectively blocked. With the increase of PA66 fiber, the porosity of alumina based ceramic core is increased, and the bending strength and line shrinkage rate at room temperature are decreased. When the PA66 fiber content is 0.9%(mass fraction), the porosity of the aluminum based ceramic core is 41.14%, the bending strength is 15.33 MPa, and the linear shrinkage rate is 0.418%.