High temperature study on the thermal properties of few-layer Mo0.5W0.5S2 and effects of capping layers

We investigated the thermal properties of few-layer Mo0.5W0.5S2 using a series of samples with different kinds of capping layers. Temperature-dependent Raman measurements were conducted in the range of 300–500 K, with power-dependent measurements also carried out. It indicated, for the few-layer Mo0.5W0.5S2, the temperature coefficients of the WS2-like E12g mode, MoS2-like E12g mode and A1g mode were −0.0155 cm−1/K, −0.0146 cm−1/K, and −0.0130 cm−1/K, respectively. And the thermal conductivity was estimated to be 44.8 W/mK. Moreover, the Mo0.5W0.5S2 samples coated with capping layers (ZrO2, HfO2) both showed a better thermal stability and a larger thermal conductivity than the one without. The results revealed that the capping layer should be an important factor in the thermal property. Keywords: Mo0.5W0.5S2, TMDs, Thermal properties, High temperature, Capping layers, Raman