Moisture dependence of positron annihilation rates in molecular substances

Positron annihilation rates have been studied in polymers and graphite-polymer composites as a function of their moisture content. The annihilation rates have been found to increase linearly with increasing moisture content in epoxies and polyamides, whereas no definite trends have been observed in polyimides. These experimental results have been used as the basis for the calculation of moisture content of several polymeric test specimens. For example, the directly measured moisture content of a Kevlar specimen was 45.5 + or - 5.0% of saturation value, whereas the moisture content on the basis of the decrease in positron lifetime was calculated to be 46.5 + or - 3.5%. Similarly, the directly measured moisture content of a graphite-epoxy composite (55 v/o fiber) was 19.2 + or - 0.6% of saturation value as opposed to a calculated value of 16.0 + or - 5.0%.