Technical Evaluation of Mechanical Recycling of PLA 3D Printing Wastes

3D printing PLA wastes were recovered from a well-known reference grade and from different sources. The recovered wastes were subjected to an energic washing step and then reprocessed into films by melt-extrusion, followed by compression molding to simulate the industrial pro-cessing conditions. The obtained materials were characterized and the optical, structural, ther-mal and crystallization behavior are reported. The mechanical recycling process leads to an in-crease of the crystallinity and a decrease of the intrinsic viscosity of the formulations, particu-larly in the sample based on blends of different 3D-PLA wastes. Moreover, the obtained films were disintegrated under composting conditions in less than one month and it was observed that recycled materials degrade somewhat faster than the starting 3D-PLA filament, as a conse-quence of the presence of shorter polymer chains. Finally, to increase the molecular weight of the recycled materials, the 3D-PLA wastes were submitted to a solid-state polymerization pro-cess at 110, 120, and 130 °C, observing that the recycled 3D-wastes materials based on a well-known reference grade experiences an improvement of the intrinsic viscosity, while that coming from different sources showed no significant changes. Thus, the results show that 3D printing PLA products provides an ideal environment for the implementation of distributed re-cycling program, in which wastes coming from well-known PLA grades can successfully be processed in films with good overall performance.