Ageing process analysis of solar panels in graveyard geostationaryorbit for reusability potential

The constant growth of space debris and the associated risks force the space community to find solutions to mitigate them. Today the most advanced solutions to dispose of satellites and rocket stages after the end of mission consists of moving them either into a graveyard orbit or towards an atmospheric re-entry ending in the demise of both spacecraft and its materials. Alternative solutions should be considered, such as providing a sustainable solution by reusing materials in space. However, it is crucial to understand better the ageing process of the materials present in currently active spacecraft and space debris. The space environment causes degradation and damage over time, making the state of those materials uncertain for potential re-use. Degradation effects have been studied as a source mechanism to result in paint flakes, ejecta particles, or delaminated insulation foils released into the space environment and sustaining a positive feedback loop through potential impacts into spacecraft. A better understanding of degradation effects would also help to better characterize the small debris environment and its evolution. The current materials databases used by the space industry could be useful tools to select materials for satellite missions with respect to their reusability, but they often do not include the evolution of material properties in space after the end of mission.This study will investigate the impact of the damage effects of radiation and meteoroid impact on solar panels. During this research, the methodology used to analyse these effects was explained. The results showed that radiation caused the most damage and could cause solar panels to lose more than a third of their performance over a period of 50 years. It was therefore possible to estimate the quantity of solar panels available for re-use. It was concluded that the results were valid, but that to obtain more accurate data, all the different types of deterioration would also have to be co
Creaternity