Search

The graphene oxide was prepared via one step under low-temperature with natural flake graphite as raw material. Factors affecting oxidation degree and layer spacing of graphene oxide were discussed in the process of low-temperature oxidation, such as the dosage of oxidant and oxidation time in system. The results indicate that high C-O bond and low defect structure (ID:IG=0.63) graphene oxide with the carbon and oxygen atom ratio of 1.98 can be prepared in the condition of the potassium permanganate with natural flake graphite mass ratio of 1:3, oxidation temperature of 0℃, oxidation time of 48h.This way avoids the increase of graphene oxide defects in the process of Hummers preparation due to the formation of CO2, which leads to the hexagon fracture and the absence of carbon atoms. After microwave reduction, the reduced graphene oxide with low defect is obtained, which the distance between defects(LD)is 12nm,the defect density(nD) is 2.21×1011cm-2 and the ratio of ID:IG is only 0.85 (ΓG=32.1cm-1).

The effects of sodium citrate on ammonium sulfate recycled leaching of low-grade zinc oxide ores were studied. By applying various kinds of detection and analysis techniques such as chemical composition analysis, chemical phase method, scanning electron microscopy and energy dispersive spectrum (SEM/EDS), X-ray diffraction (XRD) and Fourier-transforming infrared spectrum (FT-IR), zinc raw ore, its leaching slag and the functional mechanism of sodium citrate were investigated. Based on a comprehensive analysis, it can be concluded that in contrast to hemimorphite (Zn4Si2O7(OH)2 · H2O), amorphous smithsonite (ZnCO3) and zinc silicate (Zn2SiO4) prove to be refractory phases under ammonium sulfate leaching, while sodium citrate has a better chelating action with the refractory phases, resulting in a higher zinc leaching rate. Under conditions of [NH3]/[NH3]T molar ratio being 0.5, [NH3]T being 7.5 mol/L, [Na3C6H5O7] being 0.2 mol/L, S/L ratio being 1:5, temperature being 303 K, holding time being 1 h in each of the two stages, and stirring rate being 300 rpm, the leaching rate of zinc reached 93.4%. In this article, sulfate ammonium recycled technology also reveals its unique advantage in processing low-grade zinc oxide ores accompanied by high silicon and high alkaline gangue.

Eupatorium adenophorum was utilized as raw materials for the preparation of activated carbon via microwave assisted steam activation. Influences of the three vital process parameters – activation temperature, activation duration and steam flow rate – have been assessed on the adsorption capacity and yield of Eupatorium adenophorum activated carbon (EAAC). The process parameters were optimized utilizing the Design Expert software and were identified to be an activation duration of 45 min, an activation temperature of 950 °C and a steam flow rate of 0.7 ml/min, with the resultant iodine number and yield being 1,010 mg/g and 20.13% respectively. The validity of process model to optimize the process parameters was verified using the analysis of variance (ANOVA). The key parameters that characterize quality of the porous carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1,142 m2/g, 0.84 ml/g and 3.3 nm respectively, for the sample corresponding to the optimized process conditions. Additionally the pore structure is characterized using Scanning Electron Microscope (SEM). The present work strongly supports utilization of Eupatorium adenophorum as a potential precursor through microwave heating.