Developing green and simple methods for the preparation of cellulose nanofibrils (CNFs) is of great significance. Herein, a green deep eutectic solvent (DES) system based on choline chloride (ChCl) and citric acid (CA) is employed to pretreat cellulose fibers for the preparation of CNFs. The effect of the pretreatment temperature on the chemo-physical properties of the CNFs is comprehensively investigated. A high CNFs yield of up to 84.19% can be achieved under optimized conditions. The optimal CNFs show a narrow diameter distribution and length up to several microns, high crystallinity and thermal stability, as well as excellent dispersibility in water. Furthermore, semi-transparent and flexible cellulose nanopaper (CNP) was fabricated through a facile vacuum filtration process. The optimal CNP shows high tensile strength (175.15 MPa) and toughness (7.51 MJ/m 3 ). Therefore, this work provides a sustainable and facile approach to fabricate CNFs and CNP, which can be potentially used for various high-tech applications., (Copyright © 2021. Published by Elsevier Ltd.)

Composite films of xylan and polyvinyl alcohol were produced with citric acid as a new plasticizer or a cross-linking agent. The effects of citric acid content and polyvinyl alcohol/xylan weight ratio on the mechanical properties, thermal stability, solubility, degree of swelling and water vapor permeability of the composite films were investigated. The intermolecular interactions and morphology of composite films were characterized by FTIR spectroscopy and SEM. The results indicated that polyvinyl alcohol/xylan composite films had good compatibility. With an increase in citric acid content from 10% to 50%, the tensile strength reduced from 35.1 to 11.6 MPa. However, the elongation at break increased sharply from 15.1% to 249.5%. The values of water vapor permeability ranged from 2.35 to 2.95 × 10(-7)g/(mm(2)h). Interactions between xylan and polyvinyl alcohol in the presence of citric acid become stronger, which were caused by hydrogen bond and ester bond formation among the components during film forming., (Copyright © 2013. Published by Elsevier Ltd.)