The crystal of ZnWO4 doped with Co2+ has been grown by the Czochralski technique. The orientation procedure was presented. Along the crystallographic axes, the principal coefficients of thermal expansion and absorption spectra were measured and discussed. Based on the data, the crystal field parameter 10Dq, Racah parameter B, as well as the absorption cross sections were calculated. The nonlinear dependence of optical absorption on concentration of cobalt ions was found and discussed in single crystal Co2+:ZnWO4. The results indicate that inner defects such as natural cleavage or slip faces in crystal are important in the study of optical and thermal properties.

The polarized absorption, emission spectra, and the fluorescence decay curve of Er3+ ions in the anisotropic Ca3(BO3)2 crystal were investigated at room temperature. The experimental oscillator strengths for the transitions from the ground state to excited states were compared with the theoretical electric dipole oscillator strengths calculated from the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] theory. The emission cross sections and gain cross sections of the π and σ spectra were determined for the H13∕24→H15∕24 transition of special interest for laser application.

The spectroscopic properties of GdAl3(BO3)4:Tm3+ single crystal for the Tm3+ transition near 1.9μm are presented. The absorption cross section, the emission cross section, and the potential laser gain near 1.9μm are investigated for both σ and π polarizations. The broad absorption band at about 797nm and high value of the above cross section are promising features for obtaining a laser diode pumped Tm3+ laser. The maximum emission cross sections are 1.29×10−20 and 6.60×10−20cm2 at 1.85μm for the σ and π polarizations, respectively. The potential laser gain curves indicate that more than 200nm tunability range is expected for this material.

Er3+:SrWO4 crystal of good optical quality was grown by Czochralski technique method. Polarized absorption and emission spectra of Er3+ ions in SrWO4 crystal have been investigated. The Judd-Ofelt (JO) theory was applied to the polarized absorption spectra of Er3+:SrWO4 to obtain the three JO parameters: Ω2=7.41×10−20cm2, Ω4=0.25×10−20cm2, and Ω6=1.71×10−20cm2. The radiative probabilities, radiative lifetimes, and branch ratios of Er3+:SrWO4 were calculated. The stimulated emission cross sections of the potential laser transitions at 1535nm were determined using the reciprocity method and the Fuchtbauer-Ladenberg formula, and the potential laser gain versus wavelength for the I13∕24→I15∕24 transition has been estimated and discussed.