Pr3+-doped Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 (ASL) crystal along 〈100〉 direction was successfully grown using the Czochralski technique under azote atmosphere. Absorption and emission spectra of Pr:ASL crystal have been measured at room temperature. Continuous-wave laser operation of the a-cut and c-cut Pr:ASL samples under InGaN laser diode pumping has been demonstrated. For deep red laser operation at about 726 nm, the maximum output powers achieved from a-cut sample was 92.8 mW with slope efficiency of about 11.9%, while 46.6 mW with slope efficiency of 8.0% for the c-cut sample. For red laser at about 645 nm, maximum output powers of 49.2 mW and 42.8 mW were obtained for the a-cut sample and c-cut sample, corresponding to a slope efficiency of 6.7% and 8.5%, respectively. • Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal was successfully grown using the Czochralski method. • Spectral parameters of Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal were obtained. • Red and deep red laser were demonstrated in Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal. [ABSTRACT FROM AUTHOR]

Tb 3+ -doped YAlO 3 (YAP) single crystal was grown by Czochralski (Cz) method. Based on the polarized absorption spectra, the spectroscopic parameters were calculated to be Ω 2 = 3.49 × 10 −20 cm 2 , Ω 4 = 5.87 × 10 −20 cm 2 and Ω 6 = 2.55 × 10 −20 cm 2 , and then the spontaneous transition rate, fluorescent branching ratio and radiative lifetime of 5 D 4 multiplet were obtained. The yellow emission cross sections of 5 D 4 → 7 F 4 transition were calculated to be 1.72 × 10 −22 cm 2 , 2.73 × 10 −22 cm 2 and 2.65 × 10 −22 cm 2 for a, b and c polarization, respectively. The fluorescence lifetime of the 5 D 4 multiplet was fitted to be 1.72 ms. All the data indicate that Tb:YAP crystal is a promising candidate for yellow laser operation. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]