Search

Herein, gallium nitride (GaN) samples implanted with magnesium (Mg) and fluorine (F) ions are investigated by photoluminescence (PL) measurements. In low‐temperature PL measurements, the characteristic green luminescence (GL) band attributable to nitrogen vacancies (VN) is observed in Mg‐ion‐implanted GaN. As VN are likely to act as donors, suppressing their formation is essential to realizing p‐type conductivity. The energy required for a F impurity to replace VN in GaN and eventually form F on a N site decreases when the Fermi level approaches the valence band maximum, and therefore F is employed as a subsequent implantation element to compensate for VN. The GL band peak disappears upon implanting Mg and F ions at a high temperature and adjusting the F concentration to an appropriate value. This result suggests that VN generated by Mg ion implantation can be suppressed using an element with a lower formation energy than that of VN. [ABSTRACT FROM AUTHOR]

In this work, characterizations are conducted to investigate the threshold voltage (VTH) stability of the normally‐off GaN metal–insulator–semiconductor (MIS‐) field‐effect transistor (FET) with fully recessed gate structure and highly reliable low‐pressure chemical vapor deposition SiNx gate dielectric. We conducted bias‐temperature instability (BTI) tests under both positive and negative gate bias. We demonstrated the highly stable VTH of the high‐performance MIS‐FETs with small BTI, which benefits from the effective interfacial protection layer. More specifically, combining the BTI tests and drain current 1/f noise analysis, we present extensive investigation of the physical origins of BTI. According to the experimental evidence and analysis, we ascribe the VTH instability to the trapping/detrapping of the pre‐existing trap states located at the SiNx/GaN interface and/or in the gate dielectric. [ABSTRACT FROM AUTHOR]

Integration of a photon source into the AlGaN/GaN high election mobility transistor (HEMT) platform will realize the functionality of on-chip optical pumping of deep electron traps which suppress the dynamic performances of power HEMTs. Here, we report a Schottky-on-heterojunction light-emitting diode (SoH-LED) realized on the p-doping-free lateral AlGaN/GaN heterostructure. A physical mode based on hot electron induced surface states impact ionization was proposed to explain the hole generation and injection processes in this p-doping-free SoH-LED. Since the SoH-LED shares identical epitaxial structures with HEMT, integration of SoH-LED and HEMT requires no additional epi-layers during the wafer growth and minimum process modification during device fabrication. The SoH-LED structure was seamlessly integrated into the HEMT platform as an on-chip photon source. Experiment results showed that the SoH-LED photons can effectively assist the electron de-trapping processes from both of the surface and bulk deep traps, demonstrating the feasibility of using on-chip generated photons to improve the dynamic performances of AlGaN/GaN power HEMTs. [ABSTRACT FROM AUTHOR]

Effective interface engineering techniques in III-nitride heterojunction power devices, aiming at yielding high VTH stability in insulated-gate devices and suppressed current collapse in high-voltage switching operation, are of critical significance to enhance device performance and reliability. In this work, we present an interface enhancement technology featuring in situ low-damage NH3/Ar/N2 pre-gate plasma treatment prior to the ALD-Al2O3 deposition for high-performance III-nitride MIS-HEMTs. It is manifest that this technology can effectively remove the native oxide while forming a monocrystal-like nitridation interfacial-layer (NIL) on the III-nitride surface. The Al2O3(NIL)/GaN/AlGaN/GaN MIS-heterostructures with high-quality interface exhibit well-behaved electrical characteristics, including a small subthreshold swing of ∼64 mV/dec, a small hysteresis of ∼0.09 V, tiny f/T dispersions in the C- V characteristics, and low interface trap density of ∼1 × 1012-6 × 1012 cm−2eV−1. Cross-sectional TEM micrograph of the Al2O3/III-nitride gate stack with a monocrystal-like nitridation interfacial-layer (NIL). [ABSTRACT FROM AUTHOR]