Search

Dy3+-doped CaF2-SrF2 crystals with various Dy3+ dopant concentrations were synthesized by multicrucible temperature gradient technology (MC-TGT). Dy:CaF2-SrF2 crystals were fluorite structured and crystallized in cubic F m 3 ¯ m space group, as characterized by X-ray diffraction. The crystallographic site concentration was calculated from the measured density by Archimedes' hydrostatic weighing principle. The optical transmission reached over 90% with a sample thickness of 1.0 mm. The Sellmeier dispersion formula was obtained following the measured refractive index in a mid-IR range of 1.7–11 μm. Absorption coefficients of 6.06 cm−1 and 12.71 cm−1 were obtained at 804 nm and 1094 nm in 15% Dy:CaF2-SrF2 crystal. The fluorescence spectra of 15 at.% Dy:CaF2-SrF2 showed the strongest wavelength peak at 2919 nm with a full width at half maximum (FWHM) of 267 nm under an excitation wavelength of 808 nm. The fluorescence lifetimes were illustrated for different Dy3+ dopant levels of 5%, 10% and 15%. The results indicate that the Dy:CaF2-SrF2 crystal is a promising candidate for compact mid-IR lasers. [ABSTRACT FROM AUTHOR]

Yb:CaYAlO 4 (Yb:CALYO) shaped crystal fibers with different Yb3+ doping concentration were successfully grown by the micro-pulling-down (μ -PD) method. The effect of the Yb3+ concentration on the structure, absorption, emission and lifetime was systematically studied. The strongest absorption peaks of Yb:CALYO crystal fibers are located at 977 nm for σ and π polarization. The micro-photoluminescence indicate that Yb3+ ions in CALYO single crystal fiber grown by the μ -PD method distributed evenly across a cross-section. The emission cross-section of 5 at.% Yb:CALYO crystal fiber was calculated to be 0.86 × 10−20 and 1.08 × 10−20 cm2 at 983 nm for σ and π polarizations. Benefited from the disordered structrure of CaYAlO 4 crystal, the full width at half maximum (FWHM) at 978 nm was 68.9 nm and 80.9 nm, respectively. The fluorescence lifetime of 2F 5/2 energy level of Yb:CALYO crystal fibers with concentration of 0.5 at.%, 1 at.%, 2 at.% and 5 at.% was calculated to be 435 μs, 484 μs, 514 μs and 453 μs, respectively. The experimental results show that Yb:CALYO crystal fiber is a potential laser medium for ultrashort laser operation. • Yb:CaYAlO 4 shaped crystal fibers were grown by the micro-pulling down method. • The crystal structure, polarized spectra were investigated. • The effect of Yb3+ concentration on the spectroscopic properties was evaluated. [ABSTRACT FROM AUTHOR]

In this paper, the Floating zone technique was used to grow high-quality Cr3+:YScO 3 crystals. The absorption cross-sections of the 4A 2 →4T 1 transition and 4A 2 →4T 2 transitions were calculated to be 1.71 × 10−20 cm2 at 488 nm and 0.72 × 10−20 cm2 at 666 nm, respectively. The crystal field strength Dq, Racah parameters B, and C were calculated to be 1502 cm−1, 533 cm−1, and 3362 cm−1, respectively. In the Cr3+:YScO 3 crystal, the effective phonon energy and Huang-Rhys factor S were calculated to be 284 cm−1 and 8.62, respectively. The emission cross-section at 988 nm corresponding to the 4T 2 →4A 2 transition was calculated to be 1.44 × 10−20 cm2 with full width at half maximum (FWHM) of 318 nm. All the results show that Cr3+:YScO 3 crystal has the potential to be a tunable and ultrafast laser crystal. • Cr:YScO 3 crystals were successfully grown by the Floating zone technique(FZ) method. • Broad emission spectrum with full width at half maximum (FWHM) of 318 nm in Cr:YScO 3 crystals was observed. • Spectral properties and crystal field parameters of Cr:YScO 3 crystals were investigated and analysed. [ABSTRACT FROM AUTHOR]

Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. The polarized absorption spectra, polarized luminescence spectra and fluorescence decay curve of the crystal were investigated at room temperature. The spectroscopic parameters are calculated based on Judd–Ofelt theory, the values of Ω 2,4,6 were calculated to be 3.16 × 10−20 cm2, 3.93 × 10−20 cm2, 0.91 × 10−20 cm2, respectively. The Ho:CaY 0.9 Gd 0.1 AlO 4 crystal exhibits strong emission at 2013 nm for π- and 2032 nm for σ-polarizations with stimulated emission cross section of 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2, respectively. The fluorescence lifetime of the 5I 7 level was measured to be 6.60 ms. The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. • Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. • The emission cross-section at 2013 nm and 2032 nm are 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2 for π- and σ-polarizations respectively. • The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. [ABSTRACT FROM AUTHOR]

Ho3+ and Eu3+ co-doping GdScO 3 crystal was successfully grown by special EFG method. The spectroscopic properties of the crystal were measured and analyzed. The absorption cross section was calculated to be 2.027 × 10−20 cm2 at 1161 nm. The J-O theory intensity parameters Ω t (t = 2, 4, 6), radiative transition rates, fluorescence branching ratios and radiative lifetimes were calculated. The Ho,Eu:GdScO 3 crystal has very strong emission at 2869 nm and the emission cross section was 13.524 × 10−21 cm2. The fluorescence lifetimes of the 5I 7 and 5I 6 levels were measured to be 4.457 ms and 1.265 ms. Confirmed that Eu3+ can be used as an effective deactivation ion of Ho3+ in GdScO 3 crystal. All those results show that the Ho,Eu:GdScO 3 crystal would be a potential laser material for ∼3 μm mid-infrared region. • Ho,Eu:GdScO 3 crystal was successfully grown. • The spectroscopic properties of the Ho,Eu:GdScO 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho,Eu:GdScO 3 crystal. • The energy transfer between Ho3+ and Eu3+ ions, spectroscopic characteristic of ∼3 μm emission were calculated and analyzed. [ABSTRACT FROM AUTHOR]

Ho:Lu 2 O 3 crystal was successfully grown by TGT method. The spectroscopic properties of the crystal were analyzed. The absorption cross section of Ho:Lu 2 O 3 were 0.307 × 10−20 cm2 at 1147 nm and 1.076 × 10−20 cm2 at 1929 nm. J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. The intensity parameters Ω t (t = 2,4,6), radiative transition rates, branching ratios and radiative lifetime were calculated. The Ho:Lu 2 O 3 crystal had very strong emission at 2027 nm and 2849 nm and emission cross sections were calculated to be 3.271 × 10−21 cm2 and 8.852 × 10−21 cm2, respectively. The fluorescence lifetimes of the Ho3+5I 7 and 5I 6 levels were measured to be 12.400 ms and 0.622 ms. All those results show that the Ho: Lu 2 O 3 crystal would be a potential laser material for mid-infrared region. • Ho: Lu 2 O 3 crystal was successfully grown by TGT method. • The spectroscopic properties of the Ho: Lu 2 O 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. • The gain cross-section of Ho:Lu 2 O 3 crystal for ∼2 μm region and ∼3 μm region were calculated. [ABSTRACT FROM AUTHOR]

Ho3+-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed growth (EFG) method. The spectroscopic properties of Ho:GdScO 3 crystal were investigated at room temperature. The peak absorption cross-sections were 0.33 × 10−20 cm2 and 1.24 × 10−20 cm2 at 1160 nm and 653 nm with full widths at half maximum of 171.7 nm and 11.5 nm. The peak emission cross-sections of 5I 7 →5I 8 and 5I 6 →5I 7 transitions for the crystal were 0.49 × 10−20 cm2 and 1.24 × 10−20 cm2, respectively. The fluorescence lifetimes of the 5I 6 and 5I 7 multiplets were measured to be 1.12 ms and 6.13 ms, respectively. The results show that Ho:GdScO 3 crystal is a very promising material for 3 μm laser operation. • Ho:GdScO 3 crystal was successfully grown by the edge-defined film-fed growth (EFG) method. • The structure parameters of Ho:GdScO 3 crystal were studied by X-ray diffraction (XRD). • Spectral properties and Judd-Ofelt parameters of Ho:GdScO 3 crystal were investigated and compared. [ABSTRACT FROM AUTHOR]