Search

• Highest nanoindentation strain rate reported on a polymer: 103 s−1. • Nanoindentation and micropillar compression of SU-8 polymer from 10-3 to 103 s−1. • Novel nanoindentation protocol to obtain reliable modulus and hardness at 103 s−1. • High strain rate properties of SU-8 reported for first time. In situ micropillar compression and nanoindentation were performed on photolithographically fabricated SU-8 polymer inside a scanning electron microscope (SEM), covering seven orders of strain rates from 10-3 to 103 s−1. The extracted mechanical properties – modulus, hardness, yield strength, strain rate sensitivity (SRS) exponent – were systematically compared from both microscale tests and showed excellent agreement. No change in deformation mechanism was observed at high strain rates. We report a novel experimental protocol for high strain rate nanoindentation, comprising of input profile smoothing, that minimizes resonance amplitude during unloading and allows reliable extraction of modulus and hardness using standard Oliver-Pharr analysis. To the best of our knowledge, this is the first report of mechanical properties of SU-8 beyond 1 s−1 strain rate using nanoindentation based tests. [ABSTRACT FROM AUTHOR]