Search

Novel multicomponent Nb–Ni–Ti–Zr–Co alloys with 20–55 at.% Nb were synthesized from metal powders by arc melting. The resulting alloys consist primarily of Nb-rich and eutectic body-centered (BCC) phases. The content of the eutectic BCC phase is highest for an equimolar composition, while the content of the Nb-rich BCC phase increases with Nb content in the alloy. The content of secondary phases is the highest for the alloy with 32 at.% Nb. According to ab initio calculations, hydrogen occupies tetrahedral interstitial sites in the Nb-rich phase and octahedral sites in the eutectic BCC phase. For different Nb concentrations, hydrogen-binding energies were calculated. An increase in the Nb-rich phase leads to softening of multicomponent alloys. The alloys with 20 and 32 at.% Nb demonstrate high hydrogen permeability (1.05 and 0.96 × 10−8 molH2m−1s−1Pa−0.5, respectively) at 400 °C, making them promising for hydrogen purification membrane application. Multicomponent alloys with a high Nb content (55 at.%) have low resistance to hydrogen embrittlement.

A deep surface modified TiZr layer was fabricated by high-intensity low-energy titanium ion implantation into zirconium alloy Zr-1Nb. Gas-phase hydrogenation was performed to evaluate protective properties of the modified layer against hydrogen permeation into Zr-1Nb alloy. The effects of ion implantation and hydrogen on microstructure, phase composition and elemental distribution of TiZr layer were analyzed by scanning electron microscopy, X-ray diffraction, and glow-discharge optical emission spectroscopy, respectively. It was revealed that TiZr layer (~10 μm thickness) is represented by α′ + α(TiZr) lamellar microstructure with gradient distribution of Ti through the layer depth. It was shown that the formation of TiZr layer provides significant reduction of hydrogen uptake by zirconium alloy at 400 and 500 °C. Hydrogenation of the modified layer leads to refinement of lamellar plates and formation of more homogenous microstructure. Hydrogen desorption from Ti-implanted Zr-1Nb alloy was analyzed by thermal desorption spectroscopy. Hydrogen interaction with the surface modified TiZr layer, as well as its resistance properties, are discussed.

Ti-Al-N coatings were deposited on high-speed steel substrates by filtered vacuum arc deposition (FVAD) during evaporation of aluminum and titanium cathodes. Distribution of elements, phase composition, and mechanical properties of Ti-Al-N coatings were investigated using Auger electron spectroscopy (AES), X-ray diffraction (XRD), transmission electron microscopy (TEM) and nanoindentation, respectively. Additionally, tribological tests and scratch tests of the coatings were performed. The stoichiometry of the coating changes from Ti0.6Al0.4N to Ti0.48Al0.52N with increasing aluminum arc current from 70 A to 90 A, respectively. XRD and TEM showed only face-centered cubic Ti-Al-N phase with preferred orientation of the crystallites in (220) direction with respect to the sample normal and without precipitates of AlN or intermetallics inside the coatings. Incorporation of Al into the TiN lattice caused shifting of the (220) reflex to a higher 2θ angle with increasing Al content. Low content and size of microdroplets were obtained using coaxial plasma filters, which provides good mechanical and tribological properties of the coatings. The highest value of microhardness (36 GPa) and the best wear-resistance were achieved for the coating with higher Al content, thus for Ti0.48Al0.52N. These coatings exhibit good adhesive properties up to 30 N load in the scratch tests.