The graphene oxide was prepared via one step under low-temperature with natural flake graphite as raw material. Factors affecting oxidation degree and layer spacing of graphene oxide were discussed in the process of low-temperature oxidation, such as the dosage of oxidant and oxidation time in system. The results indicate that high C-O bond and low defect structure (ID:IG=0.63) graphene oxide with the carbon and oxygen atom ratio of 1.98 can be prepared in the condition of the potassium permanganate with natural flake graphite mass ratio of 1:3, oxidation temperature of 0℃, oxidation time of 48h.This way avoids the increase of graphene oxide defects in the process of Hummers preparation due to the formation of CO2, which leads to the hexagon fracture and the absence of carbon atoms. After microwave reduction, the reduced graphene oxide with low defect is obtained, which the distance between defects(LD)is 12nm,the defect density(nD) is 2.21×1011cm-2 and the ratio of ID:IG is only 0.85 (ΓG=32.1cm-1).

Microwave and conventional heating were employed to synthesize micro-sized hematite powder from hydrous ferrous sulfate, a by-product in the process of titanium pigment manufacture. The TG/DTG analysis was used to study thermal behavior of the industrial ferrous sulfate. Therefore the temperature which was significant to product was defined. The calcination experiments were carried out to assess the effect of calcination temperature covering three different temperatures (650°C, 750°C and 850°C, respectively). X-ray powder diffraction (XRD) was used to characterize the structure of the product, while the scanning electron microscopy (SEM) was utilized to characterize the morphology of the product. Microwave calcination process resulted in a mixture of hematite and minor magnetite while a considerable amount of magnesium sulfate was detected with the conventional calcination process. The transformation from periclase to magnesium was discussed during the calcinations as well. The conventional heating resulted in porous product while the microwave heating resulted in smaller particle size.