Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. The polarized absorption spectra, polarized luminescence spectra and fluorescence decay curve of the crystal were investigated at room temperature. The spectroscopic parameters are calculated based on Judd–Ofelt theory, the values of Ω 2,4,6 were calculated to be 3.16 × 10−20 cm2, 3.93 × 10−20 cm2, 0.91 × 10−20 cm2, respectively. The Ho:CaY 0.9 Gd 0.1 AlO 4 crystal exhibits strong emission at 2013 nm for π- and 2032 nm for σ-polarizations with stimulated emission cross section of 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2, respectively. The fluorescence lifetime of the 5I 7 level was measured to be 6.60 ms. The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. • Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. • The emission cross-section at 2013 nm and 2032 nm are 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2 for π- and σ-polarizations respectively. • The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. [ABSTRACT FROM AUTHOR]

LaMgAl 11 O 19 (LMA) crystal with nominal Sm3+ concentrations of 8 at.% was grown by the Czochralski method. Polarized absorption spectra, polarized emission spectra and fluorescence decay curve of Sm:LMA crystal were recorded at room temperature. The absorption cross-sections at 404 nm were calculated to be 2.33 × 10−20 cm2 and 0.86 × 10−20 cm2 for σ and π polarization, respectively. The spontaneous transition rates, branching ratios and the radiative lifetime of the 4G 5/2 multiplet, were calculated. The Judd-Ofelt theory has been applied to evaluate the Ω t (t = 2, 4, 6) intensity parameters. The highest stimulated emission cross-sections for the 4G 5/2 → 6H 7/2 transition around 594 nm were calculated to be 1.67 × 10−21 cm2 for σ polarization and 1.15 × 10−21 cm2 for π polarization, with full width at half maximum (FWHM) of 7.68 nm and 7.27 nm, respectively. The fluorescence lifetime of the 4G 5/2 manifold was 1.84 ms. All the results show that Sm:LMA crystal would be a promising orange-red solid state laser material. • The most intensive absorption line of Sm3+ ion, suitable for 405 nm InGaN laser diode. • The rigidity of Sm:LMA crystal is higher than some host crystals. • The value Ω 2 of Sm:LMA crystal is comparable to Sm:LiYF 4. • The large parameter σ em τ of Sm3+ in LMA is beneficial for the solid state laser. [ABSTRACT FROM AUTHOR]