Search

The effect of heteroepitaxial β-(AlxGa1−x)2O3 film thickness and Al content on surface morphology was characterized to experimentally determine the critical thickness limitations of the (010) β-(AlxGa1−x)2O3/Ga2O3 heterostructure. High-resolution x-ray diffraction was used to assess the strain state of the films; reciprocal space mapping (RSM) revealed that even cracked films were still fully strained. In cracked films, diffuse scattering was observed in RSMs, indicating lattice tilting. Cracking of the films was investigated using atomic force microscopy (AFM), x-ray topography (XRT), bright-field scanning transmission electron microscopy (BF-STEM), and high-resolution transmission electron microscopy. Using both AFM and XRT, the [001] direction was observed to be the most prevalent crack direction; however, cracks were also observed in the [100] direction. In uncracked regions of the films, XRT revealed the alignment of threading dislocations along the [001] direction. Cross-sectional imaging of the crack geometry and propagation was performed using BF-STEM, and it was observed that the cracks in the [001] direction extended through the thickness of the β-(AlxGa1−x)2O3 film (∼205 nm) and a further ∼100–200 nm into the β-Ga2O3 substrate. Experimental data for critical film thickness showed good agreement with previous theoretical calculations based on the Griffith criterion for crack propagation. [ABSTRACT FROM AUTHOR]

AlGaN/GaN high electron mobility transistors on QST engineered substrates are grown with different GaN/AlGaN buffer layer thickness. The as‐grown heterostructures are evaluated for their structural quality via atomic force microscopy, high‐resolution X‐ray diffraction, Raman spectroscopy, and steady‐state thermoreflectance. Transistor devices are fabricated and evaluated via DC and pulsed electrical techniques, as well as thermoreflectance imaging. It is reported that buffer layer thickness of at least 10 μm can result in lateral high electron mobility transistors (HEMTs) with simultaneously high GaN quality, low stress, good DC electrical performance, low current collapse, and low thermal resistance. [ABSTRACT FROM AUTHOR]

The first step of a multi-cycle rapid thermal annealing process was systematically studied. The surface, structure, and optical properties of Mg implanted GaN thin films annealed at temperatures ranging from 900 to 1200 °C were investigated by Raman spectroscopy, photoluminescence, UV-visible spectroscopy, atomic force microscopy, and Nomarski microscopy. The GaN thin films are capped with two layers of in-situ metal organic chemical vapor deposition -grown AlN and annealed in 24 bar of N2 overpressure to avoid GaN decomposition. The crystal quality of the GaN improves with increasing annealing temperature as confirmed by UV-visible spectroscopy and the full widths at half maximums of the E2 and A1 (LO) Raman modes. The crystal quality of films annealed above 1100 °C exceeds the quality of the as-grown films. At 1200 °C, Mg is optically activated, which is determined by photoluminescence measurements. However, at 1200 °C, the GaN begins to decompose as evidenced by pit formation on the surface of the samples. Therefore, it was determined that the optimal temperature for the first step in a multi-cycle rapid thermal anneal process should be conducted at 1150 °C due to crystal quality and surface morphology considerations. [ABSTRACT FROM AUTHOR]

An Mg-implanted p-i-n diode was fabricated and characterized. Mg activation was achieved using the multicycle rapid thermal annealing technique with rapid heating pulses up to 1340 °C. The surface of the implanted GaN after annealing was smooth (0.94 nm RMS roughness) with growth steps evident as characterized by atomic force microscopy. The full width at half-maximum of the implanted GaN E2 Raman mode approaches that of the as-grown GaN after the annealing process, indicating that the annealing process is able to reverse most of the implantation damage. The Mg-implanted p-i-n diode exhibits rectification and a low leakage current of 0.11 μA cm−2 at a bias of −10 V. Under forward bias, light emission was observed from the p-i-n diode. The implantation and activation of Mg in a GaN-based device, demonstrated for the first time in this research, is a key enabling step for future optoelectronic and power electronic devices. Current-voltage characteristics of the Mg-implanted p-i-n diode with an inset of the device schematic. [ABSTRACT FROM AUTHOR]