Search

This work studied the feasibility of ultrasonic-assisted (US-assisted) chemical cleaning of nanofiltration (NF) membranes that fouled with inorganic scales. We carried out US-assisted acid cleaning experiments by filter arsenic-rich brackish water to investigate the influencing conditions of US-assisted cleaning technology. We first optimized the proper ultrasonic power intensity (1 W/cm 2 ) in avoiding of membrane damage. US-assisted water flushing can recover the membrane water flux by around 75%, which suggested that the removal of inorganic scales was inadequate. However, US-assisted acid cleaning is efficient for removing the inorganic scales on membrane surface, and cleaning time was significantly shortened by 1/3 to 2/3 when compared with acid cleaning. It is worth to note that US-assisted acid cleaning can be carried out at a lower pH value of 3.0, while traditional acid cleaning usually conducted at pH of 2.0.This would reduce disposal amount of chemical contaminants by up to 90%. Additionally, our investigation suggests the optimal temperature for US-assisted acid cleaning was around 30 °C. This study revealed that the US-assisted acid cleaning method is an effective and environmental-friendly method for NF membrane cleaning. [ABSTRACT FROM AUTHOR]

Membrane fouling is the main problem during the nanofiltration (NF) process of brackish water desalination due to the existence of natural organic matter, especially humic acid (HA). Moreover, the conventional membrane cleaning method would do great harm to the environment because large amount of chemicals were employed. In order to control organic fouling, a novel cleaning method via direct osmosis backwash (DOBW) by injecting high salinity (HS) solution was developed. Different operating conditions for HS-DOBW technology in the actual process were systematically investigated. The results demonstrated that there was a strong driving force to lift and sweep the foulants from the membrane surface which would be carried over to the brine. The optimal conditions in terms of HS (150 kg/m 3 NaCl solution) flow rate of 0.121 L/min were selected for the subsequent experiments. The results showed that the fouling could be almost fully reversible (more than 99.78% permeate water flux recovery), and the membrane needed to be cleaned for about 10 min because of the appearance of HA on membrane surface at the fouling time of 24 h. Most importantly, the HS-DOBW technology is very effective in keeping the membrane continuously clean and ensuring stable permeate production. [ABSTRACT FROM AUTHOR]

Abstract: Nanofiltration (NF) membranes are playing a more and more important role in brackish and seawater softening process, wastewater reclamation and other industrial separation. In this study, ultrafiltation (UF) and NF (ESNA3, Hydranautics) were assembled to an integrated membrane system (IMS) as pretreatment prior to seawater reverse osmosis (SWRO) to evaluate the NF efficiency of seawater softening. The influences of NF feed property (the feed from UF1 with 100kDa MWCO and UF2 with 20kDa MWCO, respectively), operating pressure (0.5–3.0MPa), cross-flow velocity (0.028–0.048m/s) and feed temperature (5–17°C) on the softening efficiency in terms of the NF flux and ion rejection were investigated. The results showed that the high softening efficiency of NF membrane could be achieved using UF membrane with smaller MWCO (20kDa). NF system using UF2 as pretreatment process yielded a higher flux of 61.4L/(m2 h) with Ca2+, Mg2+, SO4 2− rejection of 44.37%, 73.26% and 99.82%, respectively, under the optimum operating conditions of operating pressure at 1.5MPa, cross-flow velocity at 0.035m/s and feed temperature at 12.5°C. And, the relatively excellent selectivity of divalent ions and univalent ions can be obtained by ESNA3 membrane compared to that of other NF membranes reported in the literature, indicating that the ESNA3 membrane seems to be appropriate for seawater softening process. [Copyright &y& Elsevier]