Search

• Composite propellants (CPs) containing insensitive high-energy qy-HMX have been prepared. • The qy-HMX-based CPs has 9.64% higher heat of explosion than HMX-based one. • The burn rate of CPs containing qy-HMX is 4.38 mm·s−1 at 3 MPa, 45.9% lower than that of corresponding HMX-based one. • The average particle size of the CCPs of qy-HMX-based CPs is 71.5% lower than that of HMX-based one. Two types of qy-HMX (insensitive HMX with improved energy density, numbered 1 and 2) have been used and studied as an ingredient of HTPB-based composite propellants (CPs), and the decomposition and combustion performances have been investigated. It has been shown that the main exothermic peak temperature of blank CPs containing 21 wt% of qy-HMX-1 is 258.9 °C, which is 4.7 °C higher than that of HMX-containing one, indicating improved thermostability. The corresponding heat of explosion for blank qy-HMX-2-based CPs was measured to be 5830 J∙g−1, which is 300 J∙g−1 higher than that of HMX-based one. Interestingly, the qy-HMX-2-based CPs has higher energy density than corresponding CL-20-based ones, but it has much lower burn rate under the same pressure, e.g. 4.38 mm∙s−1 at 3 MPa for the former vs. 9.03 mm∙s−1 for the latter. Under the effect of typical conventional catalysts such as nano-CuO and nano-Fe 2 O 3 , the qy-HMX-1-based CPs showed increased heat of explosion and higher burn rate. In addition, the particle sizes of condensed combustion products (CCPs) of CPs containing qy-HMX-2 are much smaller than that of HMX-based one, where the Al 4 C 3 was produced as its unique CCPs ingredient. [ABSTRACT FROM AUTHOR]

TAGP provide strong interaction which packing RDX recrystallization, in this strategy, the high energy content and insensitive qy-RDX were obtained. • High density qy-RDX hybrid crystals have been designed and prepared under constraint of TAGP. • TAGP inhibited the growth of RDX molecules (111) and (200) planes, resulting in improved energy density. • 2D TAGP can greatly change the crystal structure of RDX thereby significantly reduced its sensitivity. In this paper, the widely used energetic material RDX had been modified with 2D high nitrogen polymer (TAGP). Various hybrid RDX crystals (qy-RDX) with higher detonation velocity and better thermostability had been obtained as a result of strong intermolecular interactions between TAGP and RDX molecules. The performance of the qy-RDX had been characterized to clarify the inherent mechanisms. It shows that the⊿ H f of qy-RDX could be largely changed in the range of 23.4 kJ kg−1 to 1343.6 kJ kg−1, whereas the density varies only from 1.81 g cm−3 to 1.86 g cm−3. The resulted detonation velocities are in the range of 8725.5 m·s−1 to 9251.8 m·s−1, depending on the content and state of the TAGP dopant. The sensitivity of the resulted qy-RDX is much better than pristine RDX due to improved crystal quality as well as higher concentration of hydrogen bonds. The impact energy is improved from 8.5 J (RDX) to 22 J (qy-RDX-1), whereas the friction sensitivity improves form 130 N to over 360 N for the same case. The E a for thermal decomposition of qy-RDX-1has reduced from 147.8 kJ mol-1 (RDX) to (124.5 kJ mol-1), since TAGP dopant could be considered as active catalytic sites after melting of RDX. [ABSTRACT FROM AUTHOR]