Search

Single-edge notched specimens of a unidirectional SiC long fibre reinforced titanium alloy, were fatigued under four point bending. The propagation behaviour of short fatigue cracks from a notch was observed on the basis of the effects of fibre bridging. The branched fatigue cracks were initiated from the notch root. The fatigue cracks propagated only in the matrix and without fibre breakage. The crack propagation rate decreased with crack extension due to the crack bridging by reinforced fibres. After fatigue testing the loading and residual stresses in the reinforced fibres were measured for the arrested cracks by the X-ray diffraction method. The longitudinal stresses in the reinforced fibres were measured using high spatial resolution synchrotron radiation. A stress map around the fatigue cracks was then successfully constructed. The longitudinal stress decreased linearly with increasing distance from a location adjacent to the wake of the matrix crack. This region of decreasing stress corresponded to the debonding area between the fibre and the matrix. The interfacial frictional stress between the matrix and the fibre could be determined from the fibre stresses. The bridging stress on the crack wake was also measured as a function of a distance from a notch root. The threshold stress intensity factor range, corrected on the basis of the shielding stress, was similar to the propagation behaviour of the monolithic matrix. Hence the main factor influencing the shielding effect in composites is fibre bridging. [ABSTRACT FROM AUTHOR]

Notched specimens of porous silicon carbide with porosity 37% were fatigued under four-point bending at frequencies of 30 and 0.3 Hz. The fatigue life expressed in terms of time was rather insensitive to the test frequency, while that expressed in terms of cycles was much shorter for the case of 0.3 Hz than for 30 Hz. A time-dependent mechanism of stress corrosion cracking was mainly responsible for crack propagation, and stress cycling enhanced the crack-propagation mechanism. The crack length was estimated from the change in compliance of the specimen. The crack-propagation curve was divided into stages I and II. In stage I, the crack-propagation rate decreased even though the applied stress intensity factor became larger with crack extension, and then turned to increase in stage II. The transition from stage I to II took place at a crack extension of around 0.8 mm. This anomalous behaviour is caused by crack-tip shielding due to microcracking and asperity contact. Fractographic observations showed that the fracture path was along the binder phase between silicon carbide particles, or more precisely along the interface between particles and binders. [ABSTRACT FROM AUTHOR]

The crack closure behaviour of microstructurally small fatigue cracks was numerically simulated by combining the crack-tip slip band model with the plasticity-induced crack closure model. A Stage II crack started to propagate from an initiated Stage I crack. When the plastic zone was constrained by the grain boundary or the adjacent grain with higher yield stresses, the crack opening stress increased with crack extension, and the effective component of the stress range decreased. The crack-tip opening displacement range (ΔCTOD), first decreased with crack extension due to the development of the residual stretch, then increased until the tip of the plastic zone reached the neighbouring grain boundary. When the plastic zone was blocked by the grain boundary, ΔCTOD began to decrease. The arrest condition of cracks was given by the threshold value of ΔCTOD. At the fatigue limit, the arrest of small cracks takes place just after the Stage II crack crosses the grain boundary when the grain boundary does not act as a barrier. Only when the grain boundary has a blocking strength and the yield stress of adjacent grains is not so high, the arrest of Stage II cracks takes place before the crack reaches the grain boundary. The fatigue limit decreases with the mean stress. The predicted relation between the fatigue limit and the mean stress is close to the modified Goodman relation. [ABSTRACT FROM AUTHOR]