Woongjin Energy Co., Ltd., Daejeon 305-509, Korea(Received November 13, 2014)(Revised November 27, 2014)(Accepted December 5, 2014)Abstract Recent studies have shown methods of improving solar cell efficiency. Especially on single crystalline siliconwafer which is high-efficiency solar cell material that has been widely studied. Interstitial oxygen (Oi) is the main impurityin the Czochralski (Cz) growing method, and excess of this can form precipitates during cell fabrication. We havedemonstrated the effect of Oi impurity and oxygen precipitation concentration of the wafer on Cz-silicon solar cell efficiency.The result showed a decrease in cell efficiency as Oi and oxygen precipitation increase. Moreover, we have found that thecritical point of [Oi] to bring higher cell efficiency is at 14.5 ppma in non-existent Bulk Micro Defect (BMD).Key wordsSolar cells, Efficiency, Czochralski silicon, Oxygen precipitation, BMD

Limiting thermal exposure time using rapid thermal processing(RTP) has emerged as promising simplified process for manufacturing of solar cell in a continuous way. This paper reports the simplification of co-firing using RTP. Actual temperature profile for co-firing after screen printing is a key issue for high-quality metal-semiconductor contact. The plateau time during the firing process were varied at for 10~16 sec. Glass frit in Ag paste etch anti-reflection layer with plateau time. Glass frit in Ag paste is important for the Ag/Si contact formation and performances of crystalline Si solar cell. We achieved 17.14% efficiency with optimum conditions.

In our report a relatively simple process for fast nano-texturing of p-type(100) CZ- silicon surface using silver catalyzed wet chemical etching in aqueous hydrofluoric acid (HF) and hydrogen peroxide solution() at room temperature. The wafers were saw-damaged by NaOH(6 wt%) at for 150s. To obtain a nano-structured black surface, a thin layer of silver with thickness of 1 - 10 nm was deposited on the surfaces by evaporation system. After this process the samples were etched in HF :

The high cost of crystalline silicon solar cells has been considered as one of the major obstacles to their terrestrial applications. Spin on doping (SOD) is presented as a useful process for the manufacturing of low cost solar cells. Phosphorus (P509) was used as an n-type emitters of solar cells. N-type emitters were formed on p-type EFG ribbon Si wafers by using a SOD at different spin speed (1,000~4,000 rpm), diffusion temperatures (), and diffusion time (5~30 min) in atmosphere. With optimum condition, we were able to achieve cell efficiency of 14.1%.