Search

This study demonstrated that polymerization behavior of plant oil-based acrylic monomers (POBMs) synthesized in one-step transesterification reaction from naturally rich in oleic acid olive, canola, and high-oleic soybean oils is associated with a varying mass fraction of polyunsaturated fatty acid fragments (linoleic (C18:2) and linolenic (C18:3) acid esters) in plant oil. Using miniemulsion polymerization, a range of stable copolymer latexes was synthesized from 60 wt.% of each POBM and styrene to determine the impact of POBM chemical composition (polyunsaturation) on thermal and mechanical properties of the resulted polymeric materials. The unique composition of each plant oil serves as an experimental tool to determine the effect of polyunsaturated fatty acid fragments on POBM polymerization behavior and thermomechanical properties of crosslinked films made from POBM-based latexes. The obtained results show that increasing polyunsaturation in the copolymers results in an enhanced crosslink density of the latex polymer network which essentially impacts the mechanical properties of the films (both Young's modulus and toughness). Maximum toughness was observed for crosslinked latex films made from 50 wt.% of each POBM in the monomer feed.

In recent years, polymer chemistry has experienced an intensive development of a new field regarding the synthesis of aliphatic and aromatic biobased monomers obtained from renewable plant sources. A one-step process for the synthesis of new vinyl monomers by the reaction of direct transesterification of plant oil triglycerides with N -(hydroxyethyl)acrylamide has been recently invented to yield plant oil-based monomers (POBMs). The features of the POBM chemical structure, containing both a polar (hydrophilic) fragment capable of electrostatic interactions, and hydrophobic acyl fatty acid moieties (C 15 -C 17 ) capable of van der Waals interactions, ensures the participation of the POBMs fragments of polymers in intermolecular interactions before and during polymerization. The use of the POBMs with different unsaturations in copolymerization reactions with conventional vinyl monomers allows for obtaining copolymers with enhanced hydrophobicity, provides a mechanism of internal plasticization and control of crosslinking degree. Synthesized latexes and latex polymers are promising candidates for the formation of hydrophobic polymer coatings with controlled physical and mechanical properties through the targeted control of the content of different POBM units with different degrees of unsaturation in the latex polymers.

To investigate the utility of acrylic monomers from various plant oils in adhesives manufacturing, 25–45 wt. % of high oleic soybean oil-based monomer (HOSBM) was copolymerized in a miniemulsion with commercially applied butyl acrylate (BA), methyl methacrylate (MMA), or styrene (St). The compositions of the resulting ternary latex copolymers were varied in terms of both "soft" (HOSBM, BA) and "rigid" (MMA or St) macromolecular fragments, while total monomer conversion and molecular weight of copolymers were determined after synthesis. For most latexes, results indicated the presence of lower and higher molecular weight fractions, which is beneficial for the material adhesive performance. To correlate surface properties and adhesive performance of HOSBM-based copolymer latexes, contact angle hysteresis (using water as a contact liquid) for each latex-substrate pair was first determined. The data showed that plant oil-based latexes exhibit a clear ability to spread and adhere once applied on the surface of materials differing by polarities, such as semicrystalline polyethylene terephthalate (PET), polypropylene (PP), bleached paperboard (uncoated), and tops coated with a clay mineral paperboard. The effectiveness of plant oil-based ternary latexes as adhesives was demonstrated on PET to PP and coated to uncoated paperboard substrates. As a result, the latexes with high biobased content developed in this study provide promising adhesive performance, causing substrate failure instead of cohesive/adhesive break in many experiments. [ABSTRACT FROM AUTHOR]

Semibatch emulsion polymerization of high oleic soybean oil-based monomer (HO-SBM), 2–ethylhexyl acrylate (2-EHA), and styrene (St) was applied to synthesize pressure-sensitive latex adhesives with up to 40 wt% of plant oil-based content. Ternary latex copolymers with similar chemical composition and broadly different molecular weight distribution (MWD) and modality were synthesized at varying temperatures and the mechanism of free-radical initiation. Conventional thermal initiation with ammonium persulphate at 80 °C and ascorbic acid/ tert -butyl hydroperoxide redox system of lower reaction temperature up to 20 °C were employed. Linear, short-chain, and long-chain branched macromolecules are formed due to chain-breaking reactions of HO-SBM (chain transfer on allyl groups) and 2-EHA (inter- and intramolecular chain transfer on the polymer). The dominant effect of chain transfer on allyl group protons and subsequent decrease in molecular weight was observed at higher reaction temperatures, while extensively branched polymer with high molecular weight was obtained at reaction temperature close to 20 °C. The effect of MWD and branching on the PSAs performance of synthesized biobased latexes was studied using loop tack and peel strength and lap shear testing and compared to two commercial PSA tapes as a benchmark. A significant increase in shear strength (up to 0.23 MPa) was observed for latex adhesives due to high molecular weight fractions, maintaining satisfactory level of tack (3–7 N) and peel (3–6 N/in). Broad MWD of the copolymers can be beneficial for providing materials with high shear strength (0.25–0.33 MPA) while preserving the significant level of tack (2–4 N) and peel strength (9–12 N/in) on both glass and steel substrates. [ABSTRACT FROM AUTHOR]