Search

In this Letter, the role of background carbon in metalorganic chemical vapor deposition (MOCVD) β-Ga2O3 growth using trimethylgallium (TMGa) as the Ga precursor was investigated. The quantitative C and H incorporations in MOCVD β-Ga2O3 thin films grown at different growth rates and temperatures were measured via quantitative secondary ion mass spectroscopy (SIMS). The SIMS results revealed both [C] and [H] increase as the TMGa molar flow rate/growth rate increases or growth temperature decreases. The intentional Si incorporation in MOCVD β-Ga2O3 thin films decreases as the growth rate increases or the growth temperature decreases. For films grown at relatively fast growth rates (GRs) (TMGa > 58 μmol/min, GR > 2.8 μm/h) or relatively low temperature (<950 °C), the [C] increases faster than that of the [H]. The experimental results from this study demonstrate the previously predicted theory—H can effectively passivate the compensation effect of C in n-type β-Ga2O3. The extracted net doping concentration from quantitative SIMS {[Si]-([C]-[H])} agrees well with the free carrier concentration measured from Hall measurement. The revealing of the role of C compensation in MOCVD β-Ga2O3 and the effect of H incorporation will provide guidance on designing material synthesis for targeted device applications. [ABSTRACT FROM AUTHOR]

This Letter reports a high performance β -Ga2O3 thin channel MOSFET with T gate and degenerately doped (n++) source/drain contacts regrown by metal organic chemical vapor deposition. Highly scaled T-gate with a gate length of 160–200 nm was fabricated to achieve enhanced RF performance and passivated with 200 nm silicon nitride. Peak drain current (ID,MAX) of 285 mA/mm and peak transconductance (gm) of 52 mS/mm were measured at 10 V drain bias with 23.5 Ω mm on resistance (RON). Metal/n++ contact resistance of 0.078 Ω mm was extracted from transfer length measurements. RON is possibly dominated by interface resistance between channel and highly doped n++ regrown layer. A gate-to-drain breakdown voltage of 192 V is measured for LGD = 355 nm resulting in average breakdown field (EAVG) of 5.4 MV/cm. This EAVG is the highest reported among all sub-micron gate length lateral FETs. Current gain cut off frequency (fT) of 11 GHz and record power gain cut off frequency (fMAX) of approximately 48 GHz were extracted from small signal measurements. fT is limited by DC-RF dispersion due to interface traps which needs further investigation. The fT·VBR product is 2.112 THz V for 192 V breakdown voltage. Device surpasses the switching figure of merit of Silicon and competitive with mature wide bandgap devices. [ABSTRACT FROM AUTHOR]

Phase pure β-(AlxGa1−x)2O3 thin films are grown on (001) oriented β-Ga2O3 substrates via metalorganic chemical vapor deposition. By systematically tuning the precursor molar flow rates, the epitaxial growth of coherently strained β-(AlxGa1−x)2O3 films is demonstrated with up to 25% Al compositions as evaluated by high resolution x-ray diffraction. The asymmetrical reciprocal space mapping confirms the growth of coherent β-(AlxGa1−x)2O3 films (x < 25%) on (001) β-Ga2O3 substrates. However, the alloy inhomogeneity with local segregation of Al along the ( 2 ̄ 01) plane is observed from atomic resolution STEM imaging, resulting in wavy and inhomogeneous interfaces in the β-(AlxGa1−x)2O3/β-Ga2O3 superlattice structure. Room temperature Raman spectra of β-(AlxGa1−x)2O3 films show similar characteristics peaks as the (001) β-Ga2O3 substrate without obvious Raman shifts for films with different Al compositions. Atom probe tomography was used to investigate the atomic level structural chemistry with increasing Al content in the β-(AlxGa1−x)2O3 films. A monotonous increase in chemical heterogeneity is observed from the in-plane Al/Ga distributions, which was further confirmed via statistical frequency distribution analysis. Although the films exhibit alloy fluctuations, n-type doping demonstrates good electrical properties for films with various Al compositions. The determined valence and conduction band offsets at β-(AlxGa1−x)2O3/β-Ga2O3 heterojunctions using x-ray photoelectron spectroscopy reveal the formation of type-II (staggered) band alignment. [ABSTRACT FROM AUTHOR]

This letter reports vacuum annealing of lateral field-plated $\beta $ -Ga2O3 MOSFETs with significant current recovery and improvement in the on-state resistance, $\text{R}_{\text {on}}$ , after Reactive Ion Etching (RIE) induced damage. We fabricate and characterize MOSFETs based on Molecular Beam Epitaxy (MBE) and Metal-Organic Chemical Vapor Deposition (MOCVD) grown $\beta $ -Ga2O3 wafers to better understand the effects of vacuum annealing. We see a clear trend of vacuum annealed devices showing no reduction in breakdown voltages, $\text{V}_{\text {br}}$ , as compared to polymer passivated MOSFETs. This trend holds for identical gate-drain separation, $\text{L}_{\text {gd}}$ , varying from $20 ~\mu \text{m}$ to $60 ~\mu \text{m}$. Devices show up to 10 times reduction in $\text{R}_{\text {on}}$ as compared to previously reported $\text{R}_{\text {on}}$ for SU-8 passivated devices. For MBE sample, $\text{V}_{\text {br}}$ of 7.16 kV for a $\text{L}_{\text {gd}}$ = $40 ~\mu \text{m}$ device, with an average field strength of 1.79 MVcm $^{{-{1}}}$ and peak drain current density of 40 mA/mm, is reported. $\text{R}_{\text {on}}$ is $897 \Omega $. mm, giving Baliga’s Figure of Merit (BFOM) as 5.71 MWcm $^{{-{2}}}$. For a $\text{L}_{\text {gd}}$ = $60 ~\mu \text{m}$ device, we report record high breakdown of 8.56 kV with BFoM of 4.9 MWcm $^{{-{2}}}$. For MOCVD grown sample, a $\text{L}_{\text {gd}}$ = $60 ~\mu \text{m}$ device has $\text{V}_{\text {br}}$ of 6.11 kV, $\text{R}_{\text {on}}$ of 1.98 $\text{k}\Omega $. mm and corresponding BFoM of 1.88 MWcm $^{{-{2}}}$. Transfer Length Method (TLM) analysis indicates incomplete post etch current recovery after vacuum annealing. [ABSTRACT FROM AUTHOR]

Epitaxial growth of κ-phase Ga2O3 thin films is investigated on c-plane sapphire, GaN- and AlN-on-sapphire, and (100) oriented yttria stabilized zirconia (YSZ) substrates via metalorganic chemical vapor deposition. The structural and surface morphological properties are investigated by comprehensive material characterization. Phase pure κ-Ga2O3 films are successfully grown on GaN-, AlN-on-sapphire, and YSZ substrates through a systematical tuning of growth parameters including the precursor molar flow rates, chamber pressure, and growth temperature, whereas the growth on c-sapphire substrates leads to a mixture of β- and κ-polymorphs of Ga2O3 under the investigated growth conditions. The influence of the crystalline structure, surface morphology, and roughness of κ-Ga2O3 films grown on different substrates are investigated as a function of precursor flow rate. High-resolution scanning transmission electron microscopy imaging of κ-Ga2O3 films reveals abrupt interfaces between the epitaxial film and the sapphire, GaN, and YSZ substrates. The growth of single crystal orthorhombic κ-Ga2O3 films is confirmed by analyzing the scanning transmission electron microscopy nanodiffraction pattern. The chemical composition, surface stoichiometry, and bandgap energies of κ-Ga2O3 thin films grown on different substrates are studied by high-resolution x-ray photoelectron spectroscopy (XPS) measurements. The type-II (staggered) band alignments at three interfaces between κ-Ga2O3 and c-sapphire, AlN, and YSZ substrates are determined by XPS, with an exception of κ-Ga2O3/GaN interface, which shows type-I (straddling) band alignment. [ABSTRACT FROM AUTHOR]

Metalorganic chemical vapor deposition (MOCVD) growths of β-Ga2O3 on on-axis (100) Ga2O3 substrates are comprehensively investigated. Key MOCVD growth parameters including growth temperature, pressure, group VI/III molar flow rate ratio, and carrier gas flow rate are mapped. The dependence of the growth conditions is correlated with surface morphology, growth rate, and electron transport properties of the MOCVD grown (100) β-Ga2O3 thin films. Lower shroud gas (argon) flow is found to enhance the surface smoothness with higher room temperature (RT) electron Hall mobility. The growth rate of the films decreases but with an increase of electron mobility as the VI/III molar flow rate ratio increases. Although no significant variation on the surface morphologies is observed at different growth temperatures, the general trend of electron Hall mobilities are found to increase with increasing growth temperature. The growth rates reduce significantly with uniform surface morphologies as the chamber pressure increases. By tuning the silane flow rate, the controllable carrier concentration of (100) β-Ga2O3 thin films between low-1017 cm−3 and low-1018 cm−3 was achieved. Under optimized growth condition, an (100) β-Ga2O3 thin film with RMS roughness value of 1.64 nm and a RT mobility of 24 cm2/Vs at a carrier concentration of 7.0 × 1017 cm−3 are demonstrated. The mobilities are primarily limited by the twin lamellae and stacking faults defects generated from the growth interface. Atomic resolution scanning transmission electron microscopy reveals the formation of twin boundary defects in the films, resulting in the degradation of crystalline quality. Results from this work provide fundamental understanding of the MOCVD epitaxy of (100) β-Ga2O3 on on-axis Ga2O3 substrates and the dependence of the material properties on growth conditions. The limitation of electron transport properties of the (100) β-Ga2O3 thin films below 25 cm2/Vs is attributed to the formation of incoherent boundaries (twin lamellae) and stacking faults grown along the on-axis (100) crystal orientation. [ABSTRACT FROM AUTHOR]

This study provides the full-bandgap evaluation of defect state distributions in beta phase gallium oxide (β-Ga2O3) grown by low-pressure chemical vapor deposition (LPCVD) on (010) β-Ga2O3 substrates at high growth of up to 20 µm/h. Deep-level optical spectroscopy and deep-level transient spectroscopy measurements applied to Ni/β-Ga2O3 Schottky diodes revealed the presence of a previously unreported defect state at EC-3.6 eV, which dominated the overall trap distribution in LPCVD grown material. However, states at EC-0.8 eV, EC-2.0 eV, and EC-4.4. eV were also detected, similar to prior studies on β-Ga2O3 grown by other methods, with similar or lower concentrations for the LPCVD samples. The EC-0.8 eV and EC-2.0 eV states were previously connected to residual Fe impurities and gallium vacancies, respectively. The total concentration of traps in the LPCVD material was on par with or lower than the state-of-the-art metal–organic chemical vapor deposition-grown materials despite the much higher growth rate, and the distribution of states showed negligible dependence on SiCl4 flow rate and doping concentration. These results demonstrate that the high growth rate of LPCVD-grown β-Ga2O3 is very promising for achieving thick, low defect density, and high-quality layers needed for multi-kV device applications. [ABSTRACT FROM AUTHOR]