Purpose: The aim of this ex vivo study was to assess the ability to remove oral biofilm by different combinations of mechanical and chemical treatments on smooth and rough titanium surfaces, as well as their impact on osteoconduction. Materials and Methods: Forty-eight sandblasted acid-etched (SLA) and 48 machined titanium disks were contaminated with oral bacterial biofilm and exposed to the following treatments: (1) titanium brush (TB), (2) TB + 40% citric acid (CA), (3) TB + 5.25% sodium hypochlorite (NaOCl), (4) air polishing with glycine powder (AP), (5) AP + 40% CA, and (6) AP + 5.25% NaOCl. Residual bacteria and chemical contamination were assessed using viable bacterial count assay, scanning electron microscopy (SEM), and x-ray spectroscopy (XPS). Human primary osteoblast (hOB) adhesion and osteocalcin (OC) release were also evaluated. Results: The microbiologic, SEM, and XPS analysis indicate a higher biofilm removal efficiency of combined mechanical-chemical treatments compared with exclusively mechanical approaches, especially on SLA surfaces. SEM analysis revealed significant alterations of surface microtopography on the disks treated with TB, while no changes were observed after AP treatment. OC release by hOBs was mainly decreased on disks treated with CA and NaOCl. Conclusion: The combination of mechanical and chemical treatments provides effective oral biofilm removal on both SLA and machined implant surfaces. NaOCl and CA may have a negative effect on osteoblasts cultured on SLA samples. [ABSTRACT FROM AUTHOR]

Chlorhexidine digluconate (CHX) has shown the ability to significantly reduce inflammation and marginal bone loss (MBL) at the 1-year follow-up but limited data exist regarding its long-term efficacy in peri-implant stability. The objective was to compare the long-term effects (5 years of follow-up) of a placebo gel (16 patients in Group A) or a 0.20% CHX gel (15 patients in Group B) used at each previous surgical and prosthetic stage. Control visits were conducted in 2022, investigating the long-term effects by biological, radiological, and clinical evaluation. The data were statistically analyzed. The research achieved a 96.7% implant success rate over five years, but 41.9% of patients did not attend annual oral hygiene check-ups. The average MBL was 1.04 ± 0.39 mm, with no significant differences between the two groups. Notably, patients who attended regular periodontal check-ups experienced significantly less MBL than those who did not (p < 0.05). At five years, direct effects of CHX were absent, with both groups showing moderate bone loss. However, the results suggest that early disinfection could enhance both short- and long-term outcomes. In fact, patients with initial minor MBL due to use of CHX, preserve this advantage also after 5 years of follow-up. Additionally, the data underscore the importance of annual check-ups in early detection and management of biological complications. [ABSTRACT FROM AUTHOR]

Chlorhexidine digluconate (CHX) has shown the ability to significantly reduce inflammation and marginal bone loss (MBL) at the 1-year follow-up but limited data exist regarding its long-term efficacy in peri-implant stability. The objective was to compare the long-term effects (5 years of follow-up) of a placebo gel (16 patients in Group A) or a 0.20% CHX gel (15 patients in Group B) used at each previous surgical and prosthetic stage. Control visits were conducted in 2022, investigating the long-term effects by biological, radiological, and clinical evaluation. The data were statistically analyzed. The research achieved a 96.7% implant success rate over five years, but 41.9% of patients did not attend annual oral hygiene check-ups. The average MBL was 1.04 ± 0.39 mm, with no significant differences between the two groups. Notably, patients who attended regular periodontal check-ups experienced significantly less MBL than those who did not (p < 0.05). At five years, direct effects of CHX were absent, with both groups showing moderate bone loss. However, the results suggest that early disinfection could enhance both short- and long-term outcomes. In fact, patients with initial minor MBL due to use of CHX, preserve this advantage also after 5 years of follow-up. Additionally, the data underscore the importance of annual check-ups in early detection and management of biological complications.

Abstract Background The aim of the current study was the evaluation of initial biofilm adhesion and development on laser-microtextured implant collar surfaces and the examination of effectivity of different biofilm management methods. Methods Initial biofilm formation was investigated on hydrophobic machined and laser-microtextured (Laser-Lok) titanium surfaces and hydrophobic machined and laser-microtextured (Laser-Lok) titanium aluminium vanadium surfaces and compared to hydrophobic smooth pickled titanium surfaces, hydrophilic smooth and acid etched titanium surfaces, hydrophobic sandblasted large grid and acid etched titanium surfaces (titanium Promote) via erythrosine staining and subsequent histomorphometrical analysis and scanning electron microscopic investigations. After decontamination procedures, performed via tooth brushing and glycine powder blasting, clean implant surface was detected via histomorphometrical analysis. Results After 24 h mean initial plaque area was detected in the following descending order: smooth pickled titanium > titanium Promote > hydrophilic smooth and acid etched titanium > Laser-Lok titanium > Laser-Lok titanium aluminium vanadium. The same order was determined after 48 h of biofilm formation. After glycine powder blasting all samples depicted almost 100% clean implant surface. After tooth brushing, Laser-Lok titanium (67.19%) and Laser-Lok titanium aluminium vanadium (69.80%) showed significantly more clean implant surface than the other structured surfaces, hydrophilic smooth and acid etched titanium (50.34%) and titanium Promote (33.89%). Smooth pickled titanium showed almost complete clean implant surface (98.84%) after tooth brushing. Conclusions Both Laser-Lok surfaces showed less initial biofilm formation after 24 and 48 h than the other implant surfaces. In combination with the significant higher clean implant surfaces after domestic decontamination procedure via tooth brushing, both Laser-Lok surfaces could be a candidate for modified implant and abutment designs, especially in transmucosal areas.

(1) Background: The aim of this study is to understand from a microscopic point of view whether bicarbonate air-abrasive powders associated with ultrasonic instruments can decontaminate nine different surfaces used for the abutment/implant junction. Fibroblast growth was carried out on decontaminated surface in order to understand if there are significative differences in terms of biocompatibility. (2) Methods: After taking samples of patient plaque, nine different surfaces were contaminated and analyzed by SEM, then their wettability was evaluated. Fibroblasts were cultured on the decontaminated surfaces to understand their ability to establish a connective tissue seal after decontamination. The results were analyzed from a statistical point of view to hypothesize a mathematical model capable of explaining the properties of the surfaces. (3) Results: A negative correlation between roughness and contamination has been demonstrated, whereas a weak correlation was observed between wettability and decontamination capacity. All surfaces were topographically damaged after the decontamination treatment. Grade 5 titanium surfaces appear tougher, whereas anodized surfaces tend to lose the anodizing layer. (4) Conclusions: further studies will be needed to fully understand how these decontaminated surfaces affect the adhesion, proliferation and differentiation of fibroblasts and osteoblasts. [ABSTRACT FROM AUTHOR]

Background: The aim of the current study was the evaluation of initial biofilm adhesion and development on laser-microtextured implant collar surfaces and the examination of effectivity of different biofilm management methods. Methods: Initial biofilm formation was investigated on hydrophobic machined and laser-microtextured (Laser-Lok) titanium surfaces and hydrophobic machined and laser-microtextured (Laser-Lok) titanium aluminium vanadium surfaces and compared to hydrophobic smooth pickled titanium surfaces, hydrophilic smooth and acid etched titanium surfaces, hydrophobic sandblasted large grid and acid etched titanium surfaces (titanium Promote) via erythrosine staining and subsequent histomorphometrical analysis and scanning electron microscopic investigations. After decontamination procedures, performed via tooth brushing and glycine powder blasting, clean implant surface was detected via histomorphometrical analysis. Results: After 24 h mean initial plaque area was detected in the following descending order: smooth pickled titanium > titanium Promote > hydrophilic smooth and acid etched titanium > Laser-Lok titanium > Laser-Lok titanium aluminium vanadium. The same order was determined after 48 h of biofilm formation. After glycine powder blasting all samples depicted almost 100% clean implant surface. After tooth brushing, Laser-Lok titanium (67.19%) and Laser-Lok titanium aluminium vanadium (69.80%) showed significantly more clean implant surface than the other structured surfaces, hydrophilic smooth and acid etched titanium (50.34%) and titanium Promote (33.89%). Smooth pickled titanium showed almost complete clean implant surface (98.84%) after tooth brushing. Conclusions: Both Laser-Lok surfaces showed less initial biofilm formation after 24 and 48 h than the other implant surfaces. In combination with the significant higher clean implant surfaces after domestic decontamination procedure via tooth brushing, both Laser-Lok surfaces could be a candidate for modified implant and abutment designs, especially in transmucosal areas. [ABSTRACT FROM AUTHOR]

Dental implant is being considered successful if the patient is pleased with both of its functional and esthetic outcome. As implant complications (such as peri-implantitis, inappropriate implant position, wrong angulation, and implant location too close to anatomical structures) have been frequently encountered in dental practice, therefore, thorough knowledge to manage such complications is the key prerequisite to prevent the failure of implant. The present case report discussed the etiology, diagnosis of early peri-implantitis, and periodontal abscess with their successful management through periodontal regeneration and diode laser-assisted therapy.

C-range Ultraviolet (UVC) mercury (Hg)-vapor lamps have shown the successful decontamination of hydrocarbons and antimicrobial effects from titanium surfaces. This study focused on surface chemistry modifications of titanium dental implants by using two different light sources, Hg-vapor lamps and Light Emitting Diodes (LEDs), so as to compare the effectivity of both photofunctionalization technologies. Two different devices, a small Hg-vapor lamp (λ = 254 nm) and a pair of closely placed LEDs (λ = 278 nm), were used to irradiate the implants for 12 min. X-ray Photoelectron Spectroscopy (XPS) was employed to characterize the chemical composition of the surfaces, analysing the samples before and after the lighting treatment, performing a wide and narrow scan around the energy peaks of carbon, oxygen and titanium. XPS analysis showed a reduction in the concentration of surface hydrocarbons in both UVC technologies from around 26 to 23.4 C at.% (carbon atomic concentration). Besides, simultaneously, an increase in concentration of oxygen and titanium was observed. LED-based UVC photofunctionalization has been suggested to be as effective a method as Hg-vapor lamps to remove the hydrocarbons from the surface of titanium dental implants. Therefore, due to the increase in worldwide mercury limitations, LED-based technology could be a good alternative decontamination source.

Dental implant is being considered successful if the patient is pleased with both of its functional and esthetic outcome. As implant complications (such as peri-implantitis, inappropriate implant position, wrong angulation, and implant location too close to anatomical structures) have been frequently encountered in dental practice, therefore, thorough knowledge to manage such complications is the key prerequisite to prevent the failure of implant. The present case report discussed the etiology, diagnosis of early peri-implantitis, and periodontal abscess with their successful management through periodontal regeneration and diode laser-assisted therapy. [ABSTRACT FROM AUTHOR]

Abstract: The number of osseointegrated dental implants is increasing. Healthy peri-implant soft and hard tissues are required for the stability and survival of dental implants. In this paper we review factors that lead to peri-implant mucositis and peri-implantitis, and review treatment. [Copyright &y& Elsevier]

Peri-implantitis is a major cause of dental implant failure. Bacterial biofilm contamination on the implant induces surrounding bone resorption and soft tissue inflammation, leading to severe deterioration of oral health. However, conventional biofilm removal procedures, such as mechanical decontamination and antiseptic application, are not effective enough to induce reosseointegration on decontaminated implant surfaces. This is due to (1) incomplete decontamination of the biofilm from inaccessible areas and (2) physicochemical alteration of implant surfaces caused by decontamination procedures. Herein, a safe and effective therapeutic approach for peri-implantitis is developed, which involves decontamination of implant-bound biofilms using the kinetic energy of microsized oxygen bubbles generated from the catalytic reaction between hydrogen peroxide (H 2 O 2 ) and manganese oxide (MnO 2 ) nanozyme sheet-doped silica diatom microparticles (Diatom Microbubbler, DM). Rapidly moving microsized DM particles are able to penetrate narrow spaces between implant screws, exerting just the right amount of force to entirely destroy biofilms without harming the surrounding mucosa or implant surfaces, as opposed to conventional antiseptics such as chlorhexidine or 3% H 2 O 2 when used alone. Consequently, decontamination with DM facilitates successful reosseointegration on the peri-implantitis-affected implant surface. In summary, our new DM-based therapeutic approach will become a promising alternative to resolve clinically challenging aspects of peri-implantitis.

C-range Ultraviolet (UVC) mercury (Hg)-vapor lamps have shown the successful decontamination of hydrocarbons and antimicrobial effects from titanium surfaces. This study focused on surface chemistry modifications of titanium dental implants by using two different light sources, Hg-vapor lamps and Light Emitting Diodes (LEDs), so as to compare the effectivity of both photofunctionalization technologies. Two different devices, a small Hg-vapor lamp (λ = 254 nm) and a pair of closely placed LEDs (λ = 278 nm), were used to irradiate the implants for 12 min. X-ray Photoelectron Spectroscopy (XPS) was employed to characterize the chemical composition of the surfaces, analysing the samples before and after the lighting treatment, performing a wide and narrow scan around the energy peaks of carbon, oxygen and titanium. XPS analysis showed a reduction in the concentration of surface hydrocarbons in both UVC technologies from around 26 to 23.4 C at.% (carbon atomic concentration). Besides, simultaneously, an increase in concentration of oxygen and titanium was observed. LED-based UVC photofunctionalization has been suggested to be as effective a method as Hg-vapor lamps to remove the hydrocarbons from the surface of titanium dental implants. Therefore, due to the increase in worldwide mercury limitations, LED-based technology could be a good alternative decontamination source. [ABSTRACT FROM AUTHOR]

The surgical treatment of peri-implantitis is currently based on the removal of biofilms from the implant surface by primary means of mechanical and physical treatments. However, such approaches often determine some alterations of the implant surface with detrimental effects on re-osseointegration. This study aims to evaluate the effects of four different mechanical and physical treatments on titanium samples with moderately rough surface. Air powder abrasion (AP) with glycine powder, a titanium brush (TB) and a diode laser at 3 W (L3) and 4 W (L4) were tested. Surface morphology, roughness and chemical composition were then assessed by scanning electron microscope (SEM), white light interferometer and X-ray photoelectron spectroscopy (XPS), respectively. The microscopic analysis revealed significant alterations in surface morphology on TB samples, while AP and L3 had only a minor or null impact. L4 samples revealed signs of overheating due to the excessive power. Nevertheless, the overall roughness of the samples was not significantly altered in terms of roughness parameters. Similarly, surface chemical composition was not significantly affected by the treatments. Among the treatments tested in this study, air powder abrasion with glycine powder and 3 W diode laser had the lowest impact on surface physicochemical properties.