Polarity control and crystalline quality improvement of AlN thin films grown on Si(111) substrates by molecular beam epitaxy.

We attain N-polar and Al-polar AlN thin films on Si(111) substrates by plasma-assisted molecular beam epitaxy. The polarity of AlN epilayers has been validated by wet chemical etching using tetramethylammonium hydroxide and by the direct cross-sectional observation of atomic stacking under high-angle annular dark-field scanning transmission electron microscopy. For the 290 nm-thick as-grown N-polar AlN epilayer, x-ray diffraction (XRD) (002) and (102) ω rocking curve peak full width half maximums (FWHMs) are 475 and 1177 arcsec, and the surface mean square roughness (RMS) is 0.30 nm. We flipped the polarity using the metal-flux-modulation-epitaxy (MME) strategy. The MME strategy promotes anti-phase boundaries (APBs) on the { 2 2 ¯ 01 } crystalline planes instead of commonly observed lateral planar APBs in AlN epilayers. Merging of the tilted APBs at ∼50 nm leads to a complete Al-polar surface. For the 180 nm-thick Al-polar AlN epilayer, XRD (002) and (102) peak FWHMs are 1505 and 2380 arcsec, and the surface RMS is 1.41 nm. Strain analysis by XRD and Raman spectroscopy indicates a uniform tensile strain of 0.160% across the N-polar AlN epilayer surface and a strain distribution of 0.113%–1.16% through the epilayer. In contrast, the Al-polar AlN epilayer exhibits a much broader tensile strain distribution of 0.482%–2.406% along the growth direction, potentially due to the interaction of polarity inversion and strain relaxation. [ABSTRACT FROM AUTHOR]