With the aim of comparing initial Ge adsorption and desorption modes on different surface terminations of 4H–SiC(0 0 0 1) faces, 3 × 3, √3×√3R30° (R3) and 6√3×6√3R30° (6R3) reconstructions, of decreasing Si surface richness, have been prepared by standard surface preparation procedures. They are controlled by reflection high energy electron diffraction (RHEED), low energy electron diffraction and photoemission. One monolayer of Ge has been deposited similarly at room temperature on each of these three surfaces, followed by the same set of isochronal heatings at increasing temperatures up to complete Ge desorption. At each step of heating, the structural and chemical status of the Ge ad-layer has been probed. Marked differences between the Si- (3 × 3 and R3) and C-rich (6R3) terminations have been obtained. Ge wetting layers are only obtained up to 400 °C on 3 × 3 and R3 surfaces in the form of a 4 × 4 reconstruction. The wetting is more complete on the R3 surface, whose atomic structure is the closest to an ideally Si-terminated 1 × 1 SiC surface. At higher temperatures, the wetting layer stage transiets in Ge polycrystallites followed by the unexpected appearance on the 3 × 3 surface of a more ordered Si island structure. It denotes a Si clustering of the initial Si 3 × 3 excess, induced by the presence of Ge. A phase separation mechanism between Si and Ge prevails therefore over alloying by Ge supply onto a such Si-terminated 3 × 3 surface. Conversely, no wetting is obtained on the 6R3 surface and island formation of exclusively pure Ge takes place already at low temperature. These islands exhibit a better epitaxial relationship characterized by Ge(1 1 1)//SiC(0 0 0 1) and Ge〈1 1 −2〉//SiC〈1 −1 0 0〉, ascertained by a clear RHEED spot pattern. The absence of any Ge–C bond signature in the X-ray photoelectron spectroscopy Ge core lines indicates a dominant island nucleation on heterogeneous regions of the surface denuded by the 6R3 graphite pavings. Owing to the used annealing cycles, the deposited Ge amount desorbs on the three surfaces at differentiated temperatures ranging from 950 to 1200 °C. These differences probably reflect the varying morphologies formed at lower temperature on the different surfaces. Considering all these results, the use of imperfect 6R3 surfaces appears to be suited to promote the formation of pure and coherent Ge islands on SiC. [Copyright &y& Elsevier]