Search

Improvement of the AlGaN/GaN high-electron mobility transistor's (HEMT's) off -state breakdown voltage is achieved by implanting ^19\F^+ ions at an energy of 50 keV and dose of \1 \times \10^12\ \cm^-2 under the gate region using \BF3 as the source. The charge state of the implanted fluorine ions changes from positive to negative in the AlGaN/GaN structure because of fluorine's strong electronegativity. The negative-charged fluorine ions at the back side of the two-dimensional electron gas can raise the energy barrier of the GaN buffer layer under the channel, effectively blocking the current injected from the source to the high-field region of the GaN channel when the HEMT is biased at off-state. The source-injected electrons, if not blocked, could flow to the high-field region and initiate a premature three-terminal off-state breakdown in a conventional AlGaN/GaN HEMT. A 38% improvement of the three-terminal off-state breakdown voltage and 40% improvement of the power figure-of-merit VBD-off^2/Ron are achieved in the enhanced back barrier HEMT. [ABSTRACT FROM AUTHOR]

A systematic analytical investigation of the charge distribution and gate control of the normally-off GaN double-channel MOS-HEMT (DC-MOS-HEMT) is presented in this paper. Compared to conventional GaN MOS-HEMT, the DC-MOS-HEMT features a thin AlN insertion layer (AlN-ISL) below the original two dimensional electron gas (2DEG) channel, thus forming a second channel at the interface between AlN-ISL and the underlying GaN. This paper reveals the impact of the AlN-ISL on the 2DEG distribution and the gate control of the channels. The sensitivity of ${V}_{\text {th}}$ against the recess depth is also analytically studied and is found to be nearly independent of the recess depth as long as the recess is terminated in the upper channel layer. The analytical results are well supported by numerical device simulations, and the physical mechanisms behind these findings are explained along with the analytical investigations. [ABSTRACT FROM AUTHOR]

(Al)GaN recess-free normally OFF technology is developed for fabrication of high-yield lateral GaN-based power devices. The recess-free process is achieved by an ultrathin-barrier (UTB) AlGaN/GaN heterostructure that features a natural pinched-off 2-D electron gas channel. The top–down manufacturing technique overcomes the challenges in etching of AlGaN barrier with well-controlled depth and uniformity, which is especially attractive for fabrication of normally OFF GaN-based high-electron-mobility transistors (HEMTs) and metal–insulator–semiconductor HEMTs (MIS-HEMTs) on large-size Si substrate. With SiNx passivation grown by low-pressure chemical-vapor deposition, on-resistance of the UTB-AlGaN/GaN-based power devices can be significantly reduced. High-uniformity low-hysteresis normally OFF HEMTs and Al2O3/AlGaN/GaN MIS-HEMTs are successfully demonstrated on the UTB AlGaN/GaN-on-Si platform. It is also a compelling technology platform for manufacturing high-performance GaN-based lateral power diodes, and normally OFF p-(Al)GaN heterojunction field-effect transistors. [ABSTRACT FROM PUBLISHER]

Bulk traps in the high-resistivity buffer stack underneath the 2-dimensional electron gas (2DEG), which can interact with the high vertical electric field at OFF state, impose a critical challenge to the dynamic ON-resistance (RON) of AlGaN/GaN-on-Si power devices. In this paper, the impact of substrate bias polarity on carrier injection/transport and buffer-induced current collapse has been investigated by using ramped and transient back-gating characterizations as well as TCAD simulations. High voltage applied to the conductive Si substrate can modulate 2DEG conductivity through the back-gate effect, whereby the dynamics of both acceptor and donor buffer traps are identified. Distinct buffer trapping and asymmetric vertical leakage under opposite top-to-substratebias polarities have been observed, which are attributed to the fundamentally different carrier injection/transport mechanisms. It is suggested that the energy barrier at the nucleation-layer/Si interface can limit the electron injection from Si substrate into the buffer stack and consequently influence the bufferrelated current collapse. [ABSTRACT FROM AUTHOR]

The temperature dependence of current collapse (CC) in AlGaN/GaN high-electron mobility transistors on silicon substrate is studied in this paper. Devices without and with Si3N4 passivation are used to investigate the behavior of surface- and buffer-induced CC, respectively. It is found that the degree of surface-induced CC in unpassivated devices has a weak temperature dependence, which is induced by the cancelling out between enhanced carrier injection based on surface hopping and enhanced emission when the temperature is increased. On the other hand, the degree of buffer-induced CC in the Si3N4 passivated devices is reduced at higher temperature since the energy of hot electrons is reduced due to the phonon scattering and the trapping of hot electrons in the buffer is mitigated. Temperature-dependent transient measurement is also carried out to investigate the recovery process for these two type of CC. Two types of trap levels are identified in the unpassivated and Si3N4 passivated devices, respectively. The trap level $E1$ with an activation energy of 0.08 eV is supposed to be related to the surface trapping, while $E2$ with an activation energy of 0.22 eV is located in the buffer layer. [ABSTRACT FROM AUTHOR]

In this paper, a surface potential-based terminal charge and capacitance model, including parasitic components for AlGaN/GaN HEMTs is developed. First, by solving the charge control equations, the sheet charge density in the channel is modeled with a close-form expression. Then, using this result, based on the surface potential definition, the intrinsic terminal charges and capacitances are derived consistently with current model. Finally, by introducing parasitic components, the capacitances for the full structure of the HEMT devices are given. The model is evaluated step-by-step with good agreements compared with the TCAD simulations and the experimental data. Meanwhile, the effects of bulk traps and surface traps in the capacitances are analyzed. The complete model, including currents and capacitances has been implemented in i-MOS platform for evaluations and circuit simulations. [ABSTRACT FROM PUBLISHER]

In this paper, we investigate the enhancement-mode (E-mode) LaLuO3 (LLO)-AlGaN/GaN metal-insulator-semiconductor high-electron mobility transistors (MIS-HEMTs) fabricated using fluorine (F) plasma ion implantation with a gate-dielectric-first planar process. The E-mode MIS-HEMTs exhibit a threshold voltage (VTH) of 0.6 V, a peak transconductance of \sim193~mS/mm, a small hysteresis of 0.04 V in linear region characterized by a pulse-mode current-voltage measurement, and significantly suppressed current collapse under high-drain-bias switching conditions. X-ray photoelectron spectroscopy and secondary ion mass spectrometry analyses manifest that the negatively charged F ions penetrating into the (Al)GaN barrier layer serve as the primary VTH modulation mechanism, whereas the F ions in the fluorinated LLO film form chemical bonds with La/Lu atoms and become charge-neutral. The suppressed current collapse is verified as an advantageous byproduct of the F plasma ion implantation that also fluorinated the SiNx sidewalls in the vicinity of the gate electrode, and therefore, suppress electron injection to the gate-drain access region. [ABSTRACT FROM AUTHOR]

In this paper, we demonstrate a 253% improvement in the off-state breakdown voltage (BV) of the lattice-matched \In0.17\Al0.83 \N/GaN high-electron-mobility transistors (HEMTs) by using a new Schottky-contact technology. Based on this concept, the Schottky-source/drain and Schottky-source (SS) InAlN/GaN HEMTs are proposed. The proposed InAlN/GaN HEMTs with an LGD of 15 \mu\m showed a three-terminal BV of more than 600 V, while the conventional InAlN/GaN HEMTs of the same geometry showed a maximum BV of 184 V. Without using any field plate, the BV of 650 V was measured in the SS InAlN/GaN HEMTs with LGD = \15\ \mu\m, which is the highest BV ever achieved on InAlN/GaN HEMT. The corresponding specific on-resistance (Rsp, on) is as low as 3.4 \m\Omega \cdot \cm^2. A BV of 118 V was also obtained in SS InAlN/GaN HEMTs with LGD = \1\ \mu\m, which is the highest BV in GaN-based HEMTs featuring such a short LGD with GaN buffer. The improvement of the BV relies on the effective suppression of source carrier injection into the GaN buffer under the SS due to the smooth metal morphology and elimination of metal spikes in the Schottky metallization. [ABSTRACT FROM AUTHOR]